900167

UV curable resin

rapid cure

• Synonim(y): CPS 1040 UV
• Kod UNSPSC: 12162002
• NACRES: NA.23

Właściwości

• Formularz: liquid
• lepkość: 475 cP (Brookfield LDTDV-II digital viscometer with size 31 spindle)
• gęstość: 1.24 g/mL
• temp. przechowywania: 2-8°C

Opis

Opis ogólny

Storage:

• The storage temperature should not exceed 35 °C.
• Keep tightly closed. Store in a cool, dry, well-ventilated area.
• Do not expose to ultraviolet light.
• High temperatures (>80 °C), pressure, and contamination with peroxides may result in auto-polymerization of the product.
• Unstable upon depletion of inhibitor.

Zastosowanie

• Cures extremely rapidly to form a glassy, high modulus material
• Excellent for use in optical applications
• High refractive index - 1.54
• High impact absorption
• Non-yellowing
• No oxygen inhibition.
• Mechanical properties after curing:

Modulus*: 930 MPa
Strength*: 34 MPa
Elongation*: 13%
Pencil Hardness: 6H
Tack Free**: <2 min

*Test Resources: tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.
** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

Ta strona może zawierać tekst przetłumaczony maszynowo.

Informacja o środkach bezpieczeństwa

• Piktogramy: GHS08,GHS07,GHS09
• Hasło ostrzegawcze: Warning
• Zwroty wskazujące rodzaj zagrożenia: H302,H317,H373,H410
• Zwroty wskazujące środki ostrożności: P260 - P273 - P280 - P301 + P312 - P302 + P352 - P314
• Klasyfikacja zagrożeń: Acute Tox. 4 Oral - Aquatic Acute 1 - Aquatic Chronic 1 - Skin Sens. 1 - STOT RE 2
• Kod klasy składowania: 10 - Combustible liquids
• Klasa zagrożenia wodnego (WGK): WGK 3
• Temperatura zapłonu (°F): Not applicable
• Temperatura zapłonu (°C): Not applicable