In vitro evaluation of osteoconductivity and cellular response of zirconia and alumina based ceramics.

In vitro evaluation of osteoconductivity and cellular response of zirconia and alumina based ceramics.

Materials science & engineering. C, Materials for biological applications (2013-08-06)

Ajoy Kumar Pandey, Falguni Pati, Debika Mandal, Santanu Dhara, Koushik Biswas

要旨

Developed ceria/yttria stabilized zirconia and ceria/yttria stabilized zirconia toughened alumina supported formation of apatite layer when immersed in simulated body fluid without any prior surface treatment. The formed mineral layer was confirmed as hydroxyapatite through X-ray diffraction patterns. The calcium/phosphate atomic ratio obtained from energy dispersive X-ray spectroscopy was found to be little less (Ca/P=1.5) than that of pure hydroxyapatite (Ca/P=1.7) which indicates the probability of mixed type calcium-phosphate compound formation. The achieved thickness of apatite layer was estimated through a surface profilometer and as high as ~17 μm thickness was found after 28 days of soaking. The biocompatibility of the developed materials was ensured through in vitro human osteoblast like cell (MG63) culture on ceramic discs. The morphology of attached cells was characterized through scanning electron microscopy and fluorescent microscopy which show multilayered interconnected cell growth within 8 days of culture period. Moreover, differentiation of MG63 cells was evaluated through MTT assay, total protein content and alkaline phosphatase activity.

材料

製品番号

ブランド

製品内容

Sigma-Aldrich

酸化アルミニウム, Brockmann I, standard grade, activated, basic

Sigma-Aldrich

酸化アルミニウム, activated, Brockmann I, standard grade, neutral

Sigma-Aldrich

酸化ジルコニウム(IV), powder, 5 μm, 99% trace metals basis

Sigma-Aldrich

酸化アルミニウム, powder, 99.99% trace metals basis

Sigma-Aldrich

酸化アルミニウム, Brockmann I, standard grade, activated, acidic

Sigma-Aldrich

酸化アルミニウム, powder, primarily α phase, ≤10 μm avg. part. size, 99.5% trace metals basis

Sigma-Aldrich

酸化アルミニウム, nanopowder, <50 nm particle size (TEM)

Sigma-Aldrich

酸化セリウム(IV), nanopowder, <25 nm particle size (BET)

Sigma-Aldrich

酸化ジルコニウム(IV), nanopowder, <100 nm particle size (TEM)

Sigma-Aldrich

酸化アルミニウム, nanoparticles, <50 nm particle size (DLS), 20 wt. % in isopropanol

Sigma-Aldrich

酸化セリウム(IV), powder, <5 μm, 99.9% trace metals basis

Sigma-Aldrich

酸化アルミニウム, Corundum, α-phase, -100 mesh

Sigma-Aldrich

酸化セリウム(IV), ≥99.0%

Sigma-Aldrich

酸化アルミニウム, pellets, 3 mm

Sigma-Aldrich

酸化セリウム(IV), nanopowder, <50 nm particle size (BET), 99.95% trace rare earth metals basis

Sigma-Aldrich

酸化アルミニウム, fused, powder, primarily α-phase, -325 mesh

Sigma-Aldrich

酸化アルミニウム, nanopowder, 13 nm primary particle size (TEM), 99.8% trace metals basis

Sigma-Aldrich

ジルコニウム, powder, −100 mesh

Sigma-Aldrich

酸化アルミニウム, 99.997% trace metals basis

Sigma-Aldrich

酸化アルミニウム, Type WN-6, Neutral, Activity Grade Super I

Sigma-Aldrich

酸化アルミニウム, pore size 58 Å, ~150 mesh

Sigma-Aldrich

酸化アルミニウム, nanoparticles, 30-60 nm particle size (TEM), 20 wt. % in H₂O

Sigma-Aldrich

酸化セリウム(IV), nanoparticles, <25 nm particle size, 10 wt. % in H₂O

Sigma-Aldrich

酸化セリウム(IV), powder, 99.995% trace metals basis

Sigma-Aldrich

酸化アルミニウム, fused, powder, primarily α-phase, 100-200 mesh

Sigma-Aldrich

酸化ジルコニウム(IV), 99.99% trace metals basis (purity excludes ~2% HfO₂)

Sigma-Aldrich

ジルコニウム, foil, thickness 0.1 mm, 99.98% trace metals basis

Sigma-Aldrich

酸化アルミニウム, single crystal substrate, <0001>

Sigma-Aldrich

酸化アルミニウム, nanowires, diam. × L 2-6 nm × 200-400 nm

Sigma-Aldrich

酸化アルミニウム、メソポーラス, MSU-X (wormhole), average pore size 3.8 nm