643262

Sigma-Aldrich

Gold coated silicon wafer

99.999% (Au), layer thickness 1000 Å, 99.99% (Ti)

Sinonimo/i:

gold coated silicon, gold coated wafer

Autenticatiper visualizzare i prezzi riservati alla tua organizzazione & contrattuali
Tutte le immagini(1)

About This Item

Formula condensata:
Au
Peso molecolare:
196.97
Numero MDL:
MFCD00003436
Codice UNSPSC:
12352103
ID PubChem:
329759955
NACRES:
NA.23

Saggio

99.99% (Ti)
99.999% (Au)

diam. × spessore

4 in. × 500 μm

Spessore strato

1000 Å

Gruppi immobilizzati alla matrice

Titanium, as adhesion layer used to bind the gold to the silicon wafer.

Stringa SMILE

[Au]

InChI

1S/Au
PCHJSUWPFVWCPO-UHFFFAOYSA-N

Categorie correlate

Descrizione generale

Our gold-coated silicon wafers use electron-beam lithography to form amorphous layers (50Å of titanium followed by 1000Å of gold) on top of the silicon wafer.
The product is highly crystalline, with <111> orientation gold and <100> orientation silicon wafer is used. Titanium is used as an adhesion layer to bind gold to the silicon wafer.

Applicazioni

Gold coated silicon wafers may be used in soft lithography for micro and nanoscale patterning.

Confezionamento

Packaging 1 set in single wafer shipper

Codice della classe di stoccaggio

11 - Combustible Solids

Classe di pericolosità dell'acqua (WGK)

WGK 3

Punto d’infiammabilità (°F)

Not applicable

Punto d’infiammabilità (°C)

Not applicable

Certificati d'analisi (COA)

Cerca il Certificati d'analisi (COA) digitando il numero di lotto/batch corrispondente. I numeri di lotto o di batch sono stampati sull'etichetta dei prodotti dopo la parola ‘Lotto’ o ‘Batch’.

Possiedi già questo prodotto?

I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.

Visita l’Archivio dei documenti

I clienti hanno visto anche

Slide 1 of 7

1 of 7

Silicon wafer (single side polished), &#60;100&#62;, P-type, contains boron as dopant, diam. × thickness 3&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647764

Silicon

Silicon wafer (single side polished), &#60;111&#62;, N-type, contains no dopant, diam. × thickness 2&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647101

Silicon

Silicon wafer (single side polished), &#60;100&#62;, P-type, contains boron as dopant, diam. × thickness 2&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647675

Silicon

Silicon wafer (single side polished), &#60;111&#62;, N-type, contains phosphorus as dopant, diam. × thickness 2&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647799

Silicon

Silicon wafer (single side polished), &#60;111&#62;, N-type, contains no dopant, diam. × thickness 3&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647543

Silicon

Silicon wafer (single side polished), &#60;100&#62;, N-type, contains phosphorus as dopant, diam. × thickness 3&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647802

Silicon

Silicon wafer (single side polished), &#60;100&#62;, N-type, contains phosphorus as dopant, diam. × thickness 2&#160;in. × 0.5&#160;mm

Sigma-Aldrich

647780

Silicon

Aguilar, M. et al.
Surface Science, 482-485, 935-935 (2001)

Articoli

Synthesis of Melting Gels Using Mono-Substituted and Di-Substituted Alkoxysiloxanes

Hybrid organic-inorganic sol-gel materials containing silica were first called “ORMOSILs” in 1984.

Il team dei nostri ricercatori vanta grande esperienza in tutte le aree della ricerca quali Life Science, scienza dei materiali, sintesi chimica, cromatografia, discipline analitiche, ecc..

Contatta l'Assistenza Tecnica.