The luminescent characterization of (Sr, Ca)2SiO4:Eu2+ nanopowders synthesized by a co-precipitation method.

The luminescent characterization of (Sr, Ca)2SiO4:Eu2+ nanopowders synthesized by a co-precipitation method.

Journal of nanoscience and nanotechnology (2013-07-19)

Jun Seong Lee, Young Jin Kim

ZUSAMMENFASSUNG

(Sr, Ca)2SiO4:Eu2+ nanopowders were prepared by a co-precipitation method, and then the effects of Ca2+ ions on the structural and luminescent properties were investigated. The pure Sr2SiO4:Eu2+ powders were perfectly composed of the beta-phase, whereas the substitution of Ca2+ ions led to the beta --> alpha' phase transition. The photoluminescence spectra of Sr2SiO4:Eu2+ exhibited two excitation bands at around 330 and 375 nm assigned to Eu(I) and (II) sites, respectively, resulting in two emission bands at around 473 and 543 nm. Meanwhile, the dominant peak wavelengths of the emission spectra of (Sr, Ca)2SiO4:Eu2+ could be tuned, depending on the cation ratio of Ca2+ to Sr2+. The substitution of Ca2+ ions for Sr2+ ions caused the red-shift of the emission peaks of Sr(2-x)Ca(x)SiO4:Eu2+ powders with increasing Ca2+ content (x = 0-1.0) due to the increase in the crystal field strength.

MATERIALIEN

Produktnummer

Marke

Produktbeschreibung

718467

Sigma-Aldrich

Titan(IV)-oxid, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

Titan(IV)-oxid, Anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis

420816

Sigma-Aldrich

LUDOX^® HS-40 kolloidales Siliziumdioxid, 40 wt. % suspension in H₂O

637238

Sigma-Aldrich

Siliciumdioxid, nanopowder, 10-20 nm particle size (BET), 99.5% trace metals basis

232033

Sigma-Aldrich

Titan(IV)-oxid, Anatase, powder, 99.8% trace metals basis

14021

Sigma-Aldrich

Titan(IV)-oxid, ReagentPlus^®, ≥99%

420840

Sigma-Aldrich

LUDOX^® AS-40 kolloidales Siliziumdioxid, 40 wt. % suspension in H₂O

224227

Sigma-Aldrich

Titan(IV)-oxid, Rutil, powder, <5 μm, ≥99.9% trace metals basis

748161

Sigma-Aldrich

Silicium(IV)-oxid, nanoparticles, mesoporous, 200 nm particle size, pore size 4 nm

637246

Sigma-Aldrich

Siliciumdioxid, nanopowder (spherical, porous), 5-20 nm particle size (TEM), 99.5% trace metals basis

248576

Sigma-Aldrich

Titan(IV)-oxid, Anatase, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

Titan(IV)-oxid, Rutil, nanopowder, <100 nm particle size, 99.5% trace metals basis

420778

Sigma-Aldrich

LUDOX^® TM-50 kolloidales Siliziumdioxid, 50 wt. % suspension in H₂O

718483

Sigma-Aldrich

Silicium(IV)-oxid, nanopowder, 99.8% trace metals basis

634662

Sigma-Aldrich

Titan(IV)-oxid, Mischung aus Rutil und Anatas, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

643645

Sigma-Aldrich

Siliziumdioxid, mesostrukturiert, MCM-41 type (hexagonal)

421553

Sigma-Aldrich

Silicium(IV)-oxid

420794

Sigma-Aldrich

LUDOX^® SM kolloidales Siliziumdioxid, 30 wt. % suspension in H₂O

420875

Sigma-Aldrich

LUDOX^® AM kolloidales Siliziumdioxid, 30 wt. % suspension in H₂O

700347

Sigma-Aldrich

Titan(IV)-oxid, Mischung aus Rutil und Anatas, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

420824

Sigma-Aldrich

LUDOX^® HS-30 kolloidales Siliziumdioxid, 30 wt. % suspension in H₂O

420786

Sigma-Aldrich

LUDOX^® TM-40 kolloidales Siliziumdioxid, 40 wt. % suspension in H₂O

420859

Sigma-Aldrich

LUDOX^® TMA kolloidales Siliziumdioxid, 34 wt. % suspension in H₂O

420832

Sigma-Aldrich

LUDOX^® AS-30 kolloidales Siliziumdioxid, 30 wt. % suspension in H₂O