The role of silver and gold nanoparticles in enhancing luminescence of europium complexes.

Journal of nanoscience and nanotechnology (2014-04-18)
Hongyan Zhao, Feng Song, Fengxiao Wang, Jiadong Liu, Yanling Liu, Jun Zhang, Guiyang Chen, Shujing Liu
要旨

The influence of 12 nm spherical silver nanoparticles (AgNPs) and 20 nm spherical gold nanoparticles (AuNPs) on the luminescence of europium complex Eu(TTFA)3 were studied. When 350 nm is chosen as the incident light, the maximum enhancement factor of the complexes mixed with AgNPs is about 2.5 at the wavelength of 612 nm. Besides the enhancement of the localized field, the overlap between the localized surface plasmon resonance spectra of nanoparticles and the absorption band of fluorescent molecules is another important factor for excitation field enhancement. By means of the quasi-static approximation theory, the distribution of the electric field around a single spherical metallic nanopaticle illuminated by plane wave was calculated. The simulation results show that the field enhancement effect is more obvious when the incident light is close to the resonance of the metallic nanoparticle, which could be demonstrated by our following experimental results. The distribution of the electric field under the same conditions was also simulated through the COMSOL software. The results are consistent with those of the quasi-static approximation theory.

材料
製品番号
ブランド
製品内容

Sigma-Aldrich
銀, conductive paste
Sigma-Aldrich
銀, nanopowder, <100 nm particle size, contains PVP as dispersant, 99.5% trace metals basis
Sigma-Aldrich
銀, powder, 2-3.5 μm, ≥99.9% trace metals basis
Sigma-Aldrich
銀, flakes, 10 μm, ≥99.9% trace metals basis
Sigma-Aldrich
銀, nanopowder, <150 nm particle size, 99% trace metals basis
Sigma-Aldrich
銀, wire, diam. 0.5 mm, 99.9% trace metals basis
Sigma-Aldrich
銀, powder, 5-8 μm, ≥99.9% trace metals basis
Sigma-Aldrich
金, powder, <45 μm, 99.99% trace metals basis
Sigma-Aldrich
金, nanopowder, <100 nm particle size, 99.9% trace metals basis
Sigma-Aldrich
銀, foil, thickness 0.1 mm, 99.9% trace metals basis
Sigma-Aldrich
金, powder, <10 μm, ≥99.9% trace metals basis
Sigma-Aldrich
銀, powder, <45 μm, ≥99.99% trace metals basis
Sigma-Aldrich
銀, wire, diam. 1.0 mm, 99.9% trace metals basis
Sigma-Aldrich
銀, shot, 1-3 mm, ≥99.99% trace metals basis
Sigma-Aldrich
銀, granular, >250 μm, 99.99% trace metals basis
Sigma-Aldrich
銀, foil, thickness 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
金被覆顕微鏡用スライドガラス, 99.999% (Au), layer thickness 100 Å
Sigma-Aldrich
銀, wire, diam. 0.5 mm, ≥99.99% trace metals basis
Sigma-Aldrich
銀, wire, diam. 0.25 mm, ≥99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.25 mm, ≥99.9% trace metals basis
Sigma-Aldrich
金, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
銀, powder, <250 μm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
銀, foil, thickness 0.025 mm, 99.9% trace metals basis
Sigma-Aldrich
金, evaporation slug, diam. × L 0.3 cm × 0.6 cm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
銀, wire, diam. 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
金めっき済みガラス製カバースリップ, 99.999% (Au), layer thickness 100 Å, L × W × thickness 22 mm × 22 mm × 130-170 μm, square