Preparation and photoluminescence properties of europium ions doped TiO2 nanocrystals.

Preparation and photoluminescence properties of europium ions doped TiO2 nanocrystals.

Journal of nanoscience and nanotechnology (2013-08-02)

Hai Liu, Lixin Yu

要旨

In this paper, pure and Eu3+ doped TiO2 nanocrystals (NCs) have been fabricated successfully by a two steps of sol-gel and hydrothermal methods. The microstructures, morphologies and photoluminescent properties of Eu(3+)-TiO2 were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and photoluminescence spectroscopy (PL). XRD and PL results show that the existent of rare earth can inhibit the transformation of TiO2 NCs from anatase to rutile phase and can improve the luminescence intensity of the prepared samples. The room-temperature PL emission of the as-grown samples is dominated by the 5D(0)-7F(j) transitions of Eu3+ ions. But the luminescence intensity drops dramatically when the annealing temperature reaches a relatively high degree because of the formation of the rutile phase of TiO2 NCs hosts.

材料

製品番号

ブランド

製品内容

718467

Sigma-Aldrich

酸化チタン(IV), nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, nanopowder, <25 nm particle size, 99.7% trace metals basis

14027

Sigma-Aldrich

酸化チタン(IV), puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

232033

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, powder, 99.8% trace metals basis

14021

Sigma-Aldrich

酸化チタン(IV), ReagentPlus^®, ≥99%

224227

Sigma-Aldrich

酸化チタン(IV)、ルチル, powder, <5 μm, ≥99.9% trace metals basis

248576

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

酸化チタン(IV)、ルチル, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

酸化チタン(IV)、ルチル型/アナターゼ型混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

348791

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, 99.7% trace metals basis

366994

Sigma-Aldrich

チタン, powder, <45 μm avg. part. size, 99.98% trace metals basis

267503

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.7% trace metals basis

700347

Sigma-Aldrich

酸化チタン(IV)、ルチル型/アナターゼ型混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

268496

Sigma-Aldrich

チタン, powder, −100 mesh, 99.7% trace metals basis

204757

Sigma-Aldrich

酸化チタン(IV)、ルチル, ≥99.98% trace metals basis

204730

Sigma-Aldrich

酸化チタン(IV)、ルチル, 99.995% trace metals basis

677469

Sigma-Aldrich

酸化チタン(IV), contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

268526

Sigma-Aldrich

チタン, sponge, 1-20 mm, 99.5% trace metals basis

460400

Sigma-Aldrich

チタン, wire, diam. 0.25 mm, 99.7% trace metals basis

369489

Sigma-Aldrich

チタン, foil, thickness 2.0 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

チタン, foil, thickness 0.025 mm, 99.98% trace metals basis

348805

Sigma-Aldrich

チタン, foil, thickness 0.5 mm, 99.99% trace metals basis

767506

Sigma-Aldrich

チタン, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis

460397

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, ≥99.99% trace metals basis

266035

Sigma-Aldrich

チタン, wire, diam. 1.0 mm, 99.99% trace metals basis

635057

Sigma-Aldrich

酸化チタン(IV)、ルチル, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

267481

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.99% trace metals basis

305812

Sigma-Aldrich

チタン, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

348864

Sigma-Aldrich

チタン, wire, diam. 0.5 mm, 99.99% trace metals basis

267902

Sigma-Aldrich

チタン, wire, diam. 0.81 mm, 99.7% trace metals basis