As per the supplier, for spin-coating on glass, a standard iterative solvent cleaning protocol is recommended, involving 5 minutes of sonic cleaning in acetone, ethanol, and isopropanol, followed by blow-drying with N2 between each step, and then ozone plasma treatment (medium power for 2-5 minutes) to promote adhesion. The ink is also compatible with spin-coating on Si/SiO2 substrates, which can undergo the same pre-treatment protocol. When using the spin coater, spinning a single layer at 2000-5000 rpm results in a final film thickness of 40-60 nm. To achieve thicker films, multiple layers can be applied without a baking step, which is recommended over using a lower spin speed to maintain film uniformity. With 5 coats at 2000 rpm, a 200 nm thick film is obtained after baking at 300 °C for 30 minutes in air.
900960
Graphene dispersion
for spin/spray-coating, photonic annealing
Sinonimo/i:
Conductive ink, Graphene ink
Scegli un formato
About This Item
Prodotti consigliati
Nome del prodotto
Graphene ink for spin/spray coating photonically annealable, for spin-coating, spray-coating, photonic annealing
Livello qualitativo
Stato
dispersion (black)
Caratteristiche più verdi
Design for Energy Efficiency
Learn more about the Principles of Green Chemistry.
sustainability
Greener Alternative Product
Concentrazione
1.8-3.0 wt. % solids
Resistività
0.003-0.005 Ω-cm, sample prepared by spin-coating at 2000 rpm/30 s for 5 coats, followed by thermal annealing at 300 °C in air for 30 minutes
Dimensione particelle
≤3 μm
Viscosità
2-8 mPa.s(25 °C) (1000 s-1)
P. ebollizione
78 °C (ethanol)
Densità
0.78-0.88 g/mL at 25 °C
Categoria alternativa più verde
, Enabling
Categorie correlate
Descrizione generale
Applicazioni
Spin-coating a single layer at 2000-5000 rpm yields a final film thickness of 40-60 nm. To achieve thicker films, multiple layers can be applied without a baking step. This is recommended over using a lower spin speed to maintain film uniformity. This ink should work on almost any substrate.
Electrical performance:
Following a baking step at 300 °C for 30 minutes in air, the spin-coated films exhibit sheet resistance of 300-800 Ω/sq, corresponding to a resistivity of 0.003-0.004 Ω−cm. With 5 coats at 2000 rpm, a 200 nm thick film with a sheet resistance of 160 Ω/sq. is obtained.
General guidelines:
Ethanol is recommended for cleaning up the ink and dried films, as well as dilution. Bath sonication (5-10 minutes) of the ink prior to use is recommended following extended periods of disuse.
Avvertenze
Danger
Indicazioni di pericolo
Consigli di prudenza
Classi di pericolo
Eye Dam. 1 - Flam. Liq. 2 - Skin Irrit. 2
Codice della classe di stoccaggio
3 - Flammable liquids
Classe di pericolosità dell'acqua (WGK)
WGK 1
Punto d’infiammabilità (°F)
54.5 °F - closed cup
Punto d’infiammabilità (°C)
12.5 °C - closed cup
Scegli una delle versioni più recenti:
Possiedi già questo prodotto?
I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.
I clienti hanno visto anche
-
Is there a documented recipe available for spin coating 900960, including details on the substrates it works well with (specifically regular glass slides), any pre-processing required to promote adhesion, the quantities needed, and the spin rpm-thickness characteristics?
1 answer-
Helpful?
-