  • Effect of transition metal dopants on mechanical properties and biocompatibility of zirconia ceramics.

Effect of transition metal dopants on mechanical properties and biocompatibility of zirconia ceramics.

Journal of nanoscience and nanotechnology (2013-07-19)
Gye-Jeong Oh, Sang-Won Park, Kwi-Dug Yun, Hyun-Pil Lim, Hye-Ju Son, Jeong-Tae Koh, Kyung-Ku Lee, Doh-Jae Lee, Kwang-Min Lee, John G Fisher
PMID23862482
要旨

In this study, the effect of transition metal dopants, originally added as colouring agents, on the mechanical properties and biocompatibility of sintered zirconia was investigated. This study confirmed that transition metal dopants could have a slight detrimental effect on the mechanical properties of zirconia. The addition of metal dopants did not affect the adhesion and proliferation of gingival fibroblasts.

材料
製品番号
ブランド
製品内容
230693
Sigma-Aldrich
酸化ジルコニウム(IV), powder, 5 μm, 99% trace metals basis
544760
Sigma-Aldrich
酸化ジルコニウム(IV), nanopowder, <100 nm particle size (TEM)
403296
Sigma-Aldrich
ジルコニウム, powder, −100 mesh
204994
Sigma-Aldrich
酸化ジルコニウム(IV), 99.99% trace metals basis (purity excludes ~2% HfO2)
419141
Sigma-Aldrich
ジルコニウム, foil, thickness 0.1 mm, 99.98% trace metals basis
267724
Sigma-Aldrich
ジルコニウム, rod, diam. 6.35 mm, ≥99% trace metals basis
267651
Sigma-Aldrich
ジルコニウム, sponge, ≥99% trace metals basis
643025
Sigma-Aldrich
Zirconium(IV) oxide, nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H2O
643122
Sigma-Aldrich
Zirconium(IV) oxide, nanoparticles, dispersion, <100 nm particle size (BET), 5 wt. % in H2O