769894
Resomer® LG 824 S, Poly(L-lactide-co-glycolide)
ester terminated, Lactide: Glycolide 82:18, lactide:glycolide 82:12
Sinónimos:
Resomer® LG 824 S, PLGA
Iniciar sesiónpara Ver la Fijación de precios por contrato y de la organización
About This Item
Productos recomendados
Quality Level
form
solid
feed ratio
lactide:glycolide 82:12
viscosity
1.7-2.6 dL/g
mp
157-164 °C
transition temp
Tg 54-60 °C
storage temp.
2-8°C
General description
Resomer® LG 824 S, Poly(L-lactide-co-glycolide) (PLGA), is a semicrystalline, biocompatible, bioresorbable and biodegradable material with high porosity and high surface area. It can be processed by a variety of techniques such as electrospinning, electrospraying and wet spinning.
Application
PLGA can be used in the formation of a membrane for medical applications. It can also be used as a scaffold in tissue engineering.
Legal Information
RESOMER is a registered trademark of Evonik Rohm GmbH
Storage Class
11 - Combustible Solids
wgk_germany
WGK 3
flash_point_f
Not applicable
flash_point_c
Not applicable
Certificados de análisis (COA)
Busque Certificados de análisis (COA) introduciendo el número de lote del producto. Los números de lote se encuentran en la etiqueta del producto después de las palabras «Lot» o «Batch»
¿Ya tiene este producto?
Encuentre la documentación para los productos que ha comprado recientemente en la Biblioteca de documentos.
Los clientes también vieron
Poly (l-lactide-co-glycolide) biodegradable microfibers and electrospun nanofibers for nerve tissue engineering: an in vitro study
Bini TB, et al.
J. Mater. Sci., 41(19), 6453-6459 (2006)
In vitro biocompatibility of bioresorbable polymers: poly (L, DL-lactide) and poly (L-lactide-co-glycolide)
Ignatius AA and Claes LE
Biomaterials, 17(8), 831-839 (1996)
Electrospun poly (L-lactide-co-glycolide) biodegradable polymer nanofibre tubes for peripheral nerve regeneration
Bini TB, et al.
Nanotechnology, 15(11), 1459-1459 (2004)
Poly (L-lactide-co-glycolide) microporous membranes for medical applications produced with the use of polyethylene glycol as a pore former
Krok M and Pamula E
Journal of Applied Polymer Science, 125(S2), E187-E199 (2012)
Influences of tensile load on in vitro degradation of an electrospun poly (l-lactide-co-glycolide) scaffold
Li P, et al.
Acta Biomaterialia, 6(8), 2991-2996 (2010)
Nuestro equipo de científicos tiene experiencia en todas las áreas de investigación: Ciencias de la vida, Ciencia de los materiales, Síntesis química, Cromatografía, Analítica y muchas otras.
Póngase en contacto con el Servicio técnico