934739

Sodium manganese oxide

electrode sheet, aluminum substrate, size 5 in. × 10 in.

• Sinónimos: Manganese oxide cathode, Sodium-ion battery cathode
• Fórmula empírica (notación de Hill): Na_0.44MnO₂
• Peso molecular: 97.05
• Código UNSPSC: 26111700
• NACRES: NA.21

Propiedades

• Materiales: aluminum substrate
• Nivel de calidad: 100
• grado: battery grade
• descripción: 2.5 V vs Na/Na⁺; Application: Battery Manufacturing
• Ensayo: ≥98%
• Formulario: sheet
• composición: Active material loading 8.6 mg/cm² ± 5%
• características de los productos alternativos más sostenibles: Design for Energy Efficiency; Learn more about the Principles of Green Chemistry.
• sustainability: Greener Alternative Product
• tamaño: 5 in. × 10 in.
• grosor: 16 μm , aluminum current collector; 25-50 μm ; 72-80 μm , excluding current collector
• tamaño de partícula: 1-2 μm (active material characteristic)
• capacidad: 0.90 mAh/cm2±5 % (Areal capacity)
• aplicaciones: battery manufacturing
• categoría alternativa más sostenible: Enabling

Descripción

Descripción general

Sodium manganese oxide (Na_0.44MnO₂) electrode sheet is a ready-to-use cathode for sodium-ion battery research. The film is 5 inches x 10 inches (127 mm x 254 mm) and cast single-sided on a 16 µm thick aluminum foil current collector. The composition is 90% sodium manganese oxide (Na_0.44MnO₂), 5% Poly(vinylidene fluoride) [PVDF] and 5% carbon black. The active material is tunnel-type sodium manganese oxide, which offers fast sodium ionic conductivity and high chemical stability. PVDF acts as binder due to its thermal and electrochemical stability and carbon black boosts the electronic conductivity.

We are committed to bringing you Greener Alternative Products, which adhere to one or more of The 12 Principles of Greener Chemistry. This product has been enhanced for energy efficiency. Click here for more information.

Aplicación

The primary application of our sodium manganese oxide (Na_0.44MnO₂) electrode sheet is as a cathode for sodium-ion battery research. Manganese-based compounds are widely investigated as cathode materials for rechargeable Na-ion batteries and, in particular, tunnel-type sodium manganese oxide (Na_0.44MnO₂₎ is a promising cathode material due to its high capacity, low cost, and non-toxicity. In addition, its unique tunnel structure facilitates excellent cycle and rate performance. For example, our sodium manganese oxide showed a large capacity (experimentally 110 mAh g−1 at 0.1C), even at fast charge rates (80 mAh g-1 at 5C, 72%). In addition, Na_0.44MnO₂ shows excellent stability with a variety of electrolytes including NaClO₄ and NaPF6-based organic electrolytes.

Información de seguridad

• Código de clase de almacenamiento: 13 - Non Combustible Solids
• Clase de riesgo para el agua (WGK): WGK 3
• Punto de inflamabilidad (°F): Not applicable
• Punto de inflamabilidad (°C): Not applicable