Al3+ ions dependent structural and magnetic properties of Co-Ni nano-alloys.

Al3+ ions dependent structural and magnetic properties of Co-Ni nano-alloys.

Journal of nanoscience and nanotechnology (2014-04-18)

R H Kadam, Suresh T Alone, Anil S Gaikwad, A P Birajdar, Sagar E Shirsath

要旨

Ferrite samples with a chemical formula Co0.5Ni0.5Al(x)Fe(2-x)O4 (where x = 0.0, 0.25, 0.5, 0.75 and 1.0) were synthesized by sol-gel auto-combustion method. The synthesized samples were annealed at 600 degrees C for 4 h. An analysis of X-ray diffraction (XRD) patterns reveals the formation of single phase cubic spinel structure. The lattice parameter decreased linearly with the increasing Al content x. Nano size of the powders were confirmed by the transmission electron micrographs (TEM). Particle size, bulk density decreased whereas specific surface area and porosity of the samples increased with the Al substitution. Cation distribution of constituent ions shows linear dependence of Al substitution. Based on the cation distribution obtained from XRD data, structural parameters such as lattice parameters, ionic radii of available sites and the oxygen parameter 'u' is calculated. Saturation magnetization (M(s)), magneton number (n(B)) and coercivity (H(c)) decreased with the Al substitution. Possible explanation for the observed structural and magnetic behavior with various Al content are discussed.

材料

製品番号

ブランド

製品内容

Sigma-Aldrich

ニッケル, nanopowder, <100 nm avg. part. size, ≥99% trace metals basis

Sigma-Aldrich

コバルト, powder, 2 μm particle size, 99.8% trace metals basis

Sigma-Aldrich

アルミニウム, wire, diam. 1.0 mm, 99.999% trace metals basis

Sigma-Aldrich

アルミニウム, granular, <1 mm, 99.7% trace metals basis

Sigma-Aldrich

ニッケル, powder, <50 μm, 99.7% trace metals basis

Sigma-Aldrich

アルミニウム, foil, thickness 0.25 mm, 99.999% trace metals basis

Sigma-Aldrich

コバルト, powder, <150 μm, ≥99.9% trace metals basis

Sigma-Aldrich

ニッケル, powder, <150 μm, 99.99% trace metals basis

Sigma-Aldrich

アルミニウム, pellets, 3-12 mm, 99.99% trace metals basis

Sigma-Aldrich

アルミニウム, ReagentPlus^®, beads, 5-15 mm, 99.9% trace metals basis

Sigma-Aldrich

ニッケル, foil, thickness 0.125 mm, ≥99.9%

Sigma-Aldrich

アルミニウム, foil, thickness 0.45-0.55 mm, 99.999% trace metals basis

Sigma-Aldrich

ニッケル, wire, diam. 0.25 mm, ≥99.9%

Sigma-Aldrich

コバルト, granular, 99.99% trace metals basis

Sigma-Aldrich

アルミニウム, ACS reagent, 99%, wire, wire diam. ~1.5 mm

Sigma-Aldrich

ニッケル, powder, <1 μm, 99.8% trace metals basis

Sigma-Aldrich

アルミニウム, foil, thickness 0.13 mm, ≥99.99% trace metals basis

Sigma-Aldrich

ニッケル, foil, thickness 0.5 mm, 99.98% trace metals basis

Sigma-Aldrich

アルミニウム, wire, diam. 0.58 mm, ≥99.99% trace metals basis

Sigma-Aldrich

アルミニウム, foil, thickness 8 μm, 99% trace metals basis

Sigma-Aldrich

ニッケル, foil, thickness 0.25 mm, 99.995% trace metals basis

Sigma-Aldrich

コバルト, Carbon coated magnetic, nanopowder, <50 nm particle size (TEM), ≥99%

ニッケル, pellets, 100g, max. size 10mm, 99.999%

Sigma-Aldrich

ニッケル, foil, thickness 0.1 mm, 99.98% trace metals basis

アルミニウム, rod, 1000mm, diameter 12.7mm, 99%

Sigma-Aldrich

アルミニウム, foil, thickness 1.0 mm, 99.999% trace metals basis

Sigma-Aldrich

ニッケル, rod, diam. 6.35 mm, ≥99.99% trace metals basis

Sigma-Aldrich

コバルト, pieces, 99.5% trace metals basis

Sigma-Aldrich

アルミニウム, evaporation slug, diam. × L 6.3 mm × 6.3 mm, 99.999% trace metals basis

Sigma-Aldrich

アルミニウム, pellets, 3-8 mesh, ≥99.999% trace metals basis