917826

Sigma-Aldrich

Indium tin oxide coated PEN

80% transparency, L × W × thickness 29.7 cm × 21 cm × 125 μm, sheet resistance <15 Ω/sq

Sinonimo/i:

ITO coated polyethylene naphthalate, ITO-PEN (80% transparency), PECF-IP

Autenticatiper visualizzare i prezzi riservati alla tua organizzazione & contrattuali
Tutte le immagini(1)

About This Item

Formula condensata:
In2O3 · (SnO2)x
Codice UNSPSC:
12352303
NACRES:
NA.23

Materiali

substrate (Polyethylene naphthalate (PEN) film 125 micron thick (one side coated))

Livello qualitativo

100

Resistenza foglio

<15 Ω/sq

Lungh. × largh. × spess.

29.7 cm × 21 cm × 125 μm

Trasmittanza

550 nm, 80%

Applicazioni

This product is a one-side coated, highly transparent, flexible, ITO coated PEN polymer film. It is a ready-to-use flexible, transparent conducting substrate with low sheet resistance.
This product can be used for rapid fabrication of flexible electronics such as touch screen, Perovskite solar cells, sensors, and dye-sensitized solar cells.

Pittogrammi

Health hazard
GHS08

Avvertenze

Warning

Indicazioni di pericolo

H373

Consigli di prudenza

P260 - P314 - P501

Classi di pericolo

STOT RE 2 Inhalation

Organi bersaglio

Lungs

Codice della classe di stoccaggio

11 - Combustible Solids

Classe di pericolosità dell'acqua (WGK)

WGK 3

Certificati d'analisi (COA)

Cerca il Certificati d'analisi (COA) digitando il numero di lotto/batch corrispondente. I numeri di lotto o di batch sono stampati sull'etichetta dei prodotti dopo la parola ‘Lotto’ o ‘Batch’.

Possiedi già questo prodotto?

I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.

Visita l’Archivio dei documenti

Soumen Samanta et al.
Langmuir : the ACS journal of surfaces and colloids, 30(31), 9397-9406 (2014-07-17)
In this paper, we report a simple and versatile process of electrografting the aryl multilayers onto indium tin oxide (ITO)-coated flexible poly(ethylene naphthalate) (PEN) substrates using a diazonium salt (4-pyrrolylphenyldiazonium) solution, which was generated in situ from a reaction between
Dependence of ITO-Coated Flexible Substrates in the Performance and Bending Durability of Perovskite Solar Cells.
Pandey M, et al.
Advanced Engineering Materials, 21(8), 1900288-1900288 (2019)
Photovoltaic Performance of Plastic Dye-Sensitized Electrodes Prepared by Low-Temperature Binder-Free Coating of Mesoscopic Titania.
Miyasaka T, et al.
Journal of the Electrochemical Society, 154(5) (2007)

Il team dei nostri ricercatori vanta grande esperienza in tutte le aree della ricerca quali Life Science, scienza dei materiali, sintesi chimica, cromatografia, discipline analitiche, ecc..

Contatta l'Assistenza Tecnica.