Emerging ceramic-based materials for dentistry.

Journal of dental research (2014-10-03)
I Denry, J R Kelly
摘要

Our goal is to give an overview of a selection of emerging ceramics and issues for dental or biomedical applications, with emphasis on specific challenges associated with full-contour zirconia ceramics, and a brief synopsis on new machinable glass-ceramics and ceramic-based interpenetrating phase composites. Selected fabrication techniques relevant to dental or biomedical applications such as microwave sintering, spark plasma sintering, and additive manufacturing are also reviewed. Where appropriate, the authors have added their opinions and guidance.

材料
產品編號
品牌
產品描述

Sigma-Aldrich
氧化锆(IV), powder, 5 μm, 99% trace metals basis
Sigma-Aldrich
氧化锆(IV), nanopowder, <100 nm particle size (TEM)
Sigma-Aldrich
锆, powder, −100 mesh
Sigma-Aldrich
氧化锆(IV), 99.99% trace metals basis (purity excludes ~2% HfO2)
Sigma-Aldrich
锆, foil, thickness 0.1 mm, 99.98% trace metals basis
Sigma-Aldrich
锆, rod, diam. 6.35 mm, ≥99% trace metals basis
Sigma-Aldrich
锆, sponge, ≥99% trace metals basis
Sigma-Aldrich
氧化锆(IV), nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H2O
Sigma-Aldrich
氧化锆(IV), nanoparticles, dispersion, <100 nm particle size (BET), 5 wt. % in H2O
锆, foil, 100x100mm, thickness 0.5mm, annealed, 99.2%
锆, foil, 50x50mm, thickness 0.5mm, annealed, 99.2%
锆, foil, 50x50mm, thickness 0.125mm, annealed, 99.2%
锆, foil, 50x50mm, thickness 0.25mm, annealed, 99.2%
锆, foil, 300x300mm, thickness 0.25mm, annealed, 99.2%
锆, wire reel, 0.5m, diameter 0.5mm, as drawn, 99.2%