Experimental study on a room temperature urea-SCR of NO over activated carbon fibre-supported CeO2-CuO.

Experimental study on a room temperature urea-SCR of NO over activated carbon fibre-supported CeO2-CuO.

Environmental technology (2013-07-11)

Xiao Jiang, Pei Lu, Caiting Li, Zheng Zeng, Guangming Zeng, Luping Hu, Lei Mai, Zhi Li

ABSTRACT

In order to establish a desirable method for NO reduction, selective catalytic reduction (SCR) of NO by urea-CeO2/ACF and urea-CeO2-CuO/ACF was carried out at room temperature. The experimental results showed that 10% urea-9% CeO2/ACF could yield the highest NO conversion of 85% among the series of urea-CeO2/ACF prepared. When urea-CeO2-CuO/ACF was compared with urea-CeO2/ACF, it achieved higher NO conversion to a certain degree with the addition of CuO, which was attributed to the synergistic effect between cerium and copper. The effect of the mass ratio of CeO2 and CuO was also observed. The desirable mass ratio of CeO2 and CuO was 1:1, which yielded about 90% NO conversion when ACF was loaded with 10% urea. Furthermore, the influence of O2 concentration and NO concentration was also observed. In this study, NO conversion increased with increasing O2 concentration. In addition, some samples were further characterized by BET, X-ray diffraction, X-ray photoelectron spectroscopy and Fourier transform infrared methods.

MATERIALS

Product Number

Brand

Product Description

Sigma-Aldrich

Urea solution, BioUltra, ~8 M in H₂O

Sigma-Aldrich

Copper(II) oxide, nanopowder, <50 nm particle size (TEM)

Sigma-Aldrich

Copper, foil, ≥99.8% (complexometric)

Sigma-Aldrich

Copper, beads, 2-8 mm, ≥99.99% trace metals basis

Sigma-Aldrich

Copper, foil, thickness 0.025 mm, 99.98% trace metals basis

Sigma-Aldrich

Copper, wire, diam. 1.0 mm, ≥99.9%

Sigma-Aldrich

Copper, foil, thickness 0.5 mm, 99.98% trace metals basis

Sigma-Aldrich

Copper, wire, diam. 2.0 mm, 99.999% trace metals basis

Sigma-Aldrich

Copper, wire, diam. 0.64 mm, 99.995% trace metals basis

Sigma-Aldrich

Copper(II) oxide, powder, 99.995% trace metals basis

Sigma-Aldrich

Copper, beads, 2-8 mm, 99.9995% trace metals basis

Sigma-Aldrich

Urea-¹²C, 99.9 atom % ¹²C

Sigma-Aldrich

Copper, foil, thickness 1.0 mm, 99.999% trace metals basis

Sigma-Aldrich

Copper(II) oxide, powder, 99.99% trace metals basis

Sigma-Aldrich

Copper, wire, diam. 0.25 mm, 99.999% trace metals basis

Sigma-Aldrich

Copper, powder, <75 μm, 99%

Sigma-Aldrich

Copper(II) oxide, 99.999% trace metals basis

Sigma-Aldrich

Copper, turnings, purum p.a., ≥99.0%

Sigma-Aldrich

Urea solution, 40 % (w/v) in H₂O

Sigma-Aldrich

Copper(II) oxide, needles, mixture of CuO and Cu₂O, ACS reagent

Sigma-Aldrich

Copper(II) oxide, powder, <10 μm, 98%

Millipore

Urea solution, suitable for microbiology, 40% in H₂O

Sigma-Aldrich

Copper(II) oxide, ACS reagent, ≥99.0%

Sigma-Aldrich

Copper(II) oxide on alumina, 14-30 mesh, extent of labeling: 13 wt. % loading

Sigma-Aldrich

Copper, nanopowder, 60-80 nm particle size (SAXS), ≥99.5% trace metals basis

Sigma-Aldrich

Copper, nanopowder, 40-60 nm particle size (SAXS), ≥99.5% trace metals basis

Sigma-Aldrich

Cerium(IV) oxide, nanopowder, <50 nm particle size (BET), 99.95% trace rare earth metals basis

Sigma-Aldrich

Cerium(IV) oxide, powder, <5 μm, 99.9% trace metals basis

Sigma-Aldrich

Cerium, ingot, under oil, 99.9% trace rare earth metals basis

Sigma-Aldrich

Copper, shot, −3-+14 mesh, 99%