Electron Microscopy

Scanning electron microscopy (SEM) uses a relatively low-power electron beam for imaging and interaction with the sample. Electron detectors identify secondary electrons at the surface and backscattered electrons in deeper regions. Secondary electrons are generated from inelastic interactions between the electron beam and the atoms of the sample. Backscattered electrons are generated after elastic interaction between the electron beam and the sample. SEM requires little to no sample preparation and is much faster and less restrictive than other types of electron microscopy. Large (~200 millimeter) samples can be directly imaged after mounting to a holder or stub. SEM commonly uses energy-dispersive X-ray spectroscopy (EDS or EDX) to map the distribution of elements within a sample. Electron beam-induced current (EBIC) and cathodoluminescence (CL) are other methods to analyze the high-quality images and optoelectronic properties of samples.

Transmission electron microscopy (TEM) uses a high-energy beam of electrons to transmit electrons through a sample to create a 2D image at the highest possible resolution. Nanomaterials can be analyzed through TEM to reveal their structure and composition information at the atomic level. Selecting the right sample holder (TEM grid) for different types of nanomaterials is vital to obtain the most detailed information. When samples are too thick, they must first be made thin enough for electrons to travel through them, ideally 100 nanometers or less. These TEM samples are then mounted onto a TEM grid and studied under ultrahigh vacuum conditions with a focused, intense electron beam. TEM utilizes the selected area diffraction (SAD) of electrons passing through the sample to provide crystallographic information about the sample material. Electron energy loss spectroscopy (EELS) and energy-dispersive X-ray spectroscopy (EDX) are methods of analysis to measure the atomic composition, chemical bonding, electronic properties, and local material thickness. 

Scanning transmission electron microscopy (STEM) scans a focused electron beam (with typical spot size of 0.05-0.2 nm) over the sample to complete imaging and spectroscopic mapping simultaneously, allowing direct correlation of spatial information and spectroscopic data.