Effect of model dissolved organic matter coating on sorption of phenanthrene by TiO2 nanoparticles.

Effect of model dissolved organic matter coating on sorption of phenanthrene by TiO2 nanoparticles.

Environmental pollution (Barking, Essex : 1987) (2014-08-05)

Xilong Wang, Enxing Ma, Xiaofang Shen, Xiaoying Guo, Meng Zhang, Haiyun Zhang, Ye Liu, Fei Cai, Shu Tao, Baoshan Xing

摘要

Dissolved organic matter (DOM) may alter the sorption of hydrophobic organic contaminants (HOC) to metal oxide nanoparticles (NPs), but the role of DOM and NP types is poorly understood. Here, phenanthrene sorption was quantified on four types of nano-TiO2 (three rutile, one anatase), and a bulk, raw TiO2 powder. Prior to the sorption experiments, these nanoparticles were coated using four different organic materials: Lignin (LIG), tannic acid (TAN), Congo red (CON), and capsorubin (CAP). Lignin, tannic acid, congo red and capsorubin coating substantially enhanced phenanthrene sorption to various TiO2 particles. After coating with a specific DOM, Kd values by the DOM-coated TiO2 particles on percent organic carbon content and surface area (SA) basis (Koc/SA) generally followed the order: TiO2 NPs with hydrophobic surfaces > bulk TiO2 particles > other TiO2 NPs. Different Koc/SA values of various DOM-TiO2 complexes resulted from distinct conformation of the coated DOM and aggregation.

材料

货号

品牌

产品描述

P11409

Sigma-Aldrich

菲, 98%

348791

Sigma-Aldrich

钛, foil, thickness 0.127 mm, 99.7% trace metals basis

366994

Sigma-Aldrich

钛, powder, <45 μm avg. part. size, 99.98% trace metals basis

267503

Sigma-Aldrich

钛, foil, thickness 0.25 mm, 99.7% trace metals basis

268496

Sigma-Aldrich

钛, powder, −100 mesh, 99.7% trace metals basis

48569

Supelco

菲, analytical standard, for environmental analysis

695114

Sigma-Aldrich

菲, sublimed grade, ≥99.5%

460400

Sigma-Aldrich

钛, wire, diam. 0.25 mm, 99.7% trace metals basis

268526

Sigma-Aldrich

钛, sponge, 1-20 mm, 99.5% trace metals basis

GF16031843

钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

348848

Sigma-Aldrich

钛, foil, thickness 0.025 mm, 99.98% trace metals basis

369489

Sigma-Aldrich

钛, foil, thickness 2.0 mm, 99.7% trace metals basis

GF29374005

钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

348805

Sigma-Aldrich

钛, foil, thickness 0.5 mm, 99.99% trace metals basis

767506

Sigma-Aldrich

钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis

266035

Sigma-Aldrich

钛, wire, diam. 1.0 mm, 99.99% trace metals basis

267481

Sigma-Aldrich

钛, foil, thickness 0.25 mm, 99.99% trace metals basis

460397

Sigma-Aldrich

钛, foil, thickness 0.127 mm, ≥99.99% trace metals basis

305812

Sigma-Aldrich

钛, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis

GF46592949

钛, wire, straight, 1000mm, diameter 1.0mm, as drawn, 99.6+%

GF31127712

钛, rod, 10mm, diameter 50mm, 99.99+%

GF14990935

钛, tube, 1000mm, outside diameter 10.3mm, inside diameter 8.7mm, wall thickness 0.8mm, annealed, 99.6+%

433667

Sigma-Aldrich

钛, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

GF62977540

钛, tube, 200mm, outside diameter 2.03mm, inside diameter 1.63mm, wall thickness 0.2mm, annealed, 99.6+%

267902

Sigma-Aldrich

钛, wire, diam. 0.81 mm, 99.7% trace metals basis

GF86399106

钛, tube, 500mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF13900205

钛, tube, 100mm, outside diameter 0.51mm, inside diameter 0.35mm, wall thickness 0.08mm, annealed, 99.6+%

GF49264713

钛, tube, 200mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF43519945

钛, wire reel, 2m, diameter 1.0mm, as drawn, 99.99+%