Characterisation and thermal properties of titanium dioxide nanoparticles-containing biodegradable polylactide composites synthesized by sol-gel method.

Journal of nanoscience and nanotechnology (2014-04-18)
Nikiwe Mhlanga, Suprakas Sinha Ray
摘要

This study reports the synthesis, characterisation and thermal properties of polylactide (PLA)/titanium dioxide nanoparticles (TiO2 NPs) composites using the sol-gel method. The percentage weight of TiO2 NP sol was varied from 3, 8, 11 and 14. The synthesised composites were characterised using scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction, energy dispersive X-ray spectroscopy (EDS), thermogravimetric analysis and dynamic mechanical analysis. Encapsulation of the TiO2 into the PLA matrix was attainable based on the SEM images and the FTIR and EDS results. The thermal stability of the composites was shifted to lower temperatures due to photodegradation induced by the metal oxide on the PLA chain. Both PLA and TiO2 NPs have potential in drug delivery because of their biocompatibility and biodegradability.

材料
货号
品牌
产品描述

Sigma-Aldrich
氧化钛(IV), nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis
Sigma-Aldrich
氧化钛 (IV),锐钛矿, nanopowder, <25 nm particle size, 99.7% trace metals basis
Sigma-Aldrich
氧化钛(IV), puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%
Sigma-Aldrich
氧化钛 (IV),锐钛矿, powder, 99.8% trace metals basis
Sigma-Aldrich
氧化钛(IV), ReagentPlus®, ≥99%
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, powder, <5 μm, ≥99.9% trace metals basis
Sigma-Aldrich
氧化钛 (IV),锐钛矿, powder, −325 mesh, ≥99% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, nanopowder, <100 nm particle size, 99.5% trace metals basis
Sigma-Aldrich
氧化钛(IV),金红石和锐钛矿混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis
Sigma-Aldrich
钛, powder, <45 μm avg. part. size, 99.98% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.127 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
氧化钛(IV),金红石和锐钛矿混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H2O, 99.5% trace metals basis
Sigma-Aldrich
钛, powder, −100 mesh, 99.7% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, ≥99.98% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, 99.995% trace metals basis
Sigma-Aldrich
氧化钛(IV), contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%
Sigma-Aldrich
钛, wire, diam. 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
氧化钛(IV), nanowires, diam. × L ~100 nm × 10 μm
Sigma-Aldrich
钛, sponge, 1-20 mm, 99.5% trace metals basis
Sigma-Aldrich
钛, foil, thickness 2.0 mm, 99.7% trace metals basis
Sigma-Aldrich
氧化钛(IV), nanowires, diam. × L ~10 nm × 10 μm
Sigma-Aldrich
钛, foil, thickness 0.025 mm, 99.98% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis
钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave
Sigma-Aldrich
钛, foil, thickness 0.127 mm, ≥99.99% trace metals basis
钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm