Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Journal of nanoscience and nanotechnology (2014-04-17)

D B Zhu, J P Liang, Y X Qu, G L Duan

ZUSAMMENFASSUNG

Functionalized ceramic dental crown was successfully fabricated through selective slurry extrusion (SSE) based technique of solid freeform fabrication (also known as rapid prototyping). After sintering, the decomposed tourmaline powders were embedded in ZrO2 matrix. The far infrared emission properties of the ceramic dental crown were improved due to the increase of the numbers of infrared active bonds from tourmaline. This new dental restoration process presents potential to provide dental patients with functionalized artificial teeth, which benefits the body health by the way of emitting far infrared rays in ambient temperatures.

MATERIALIEN

Produktnummer

Marke

Produktbeschreibung

Sigma-Aldrich

Zirkonium(IV)-oxid, powder, 5 μm, 99% trace metals basis

Sigma-Aldrich

Zirkonium(IV)-oxid, nanopowder, <100 nm particle size (TEM)

Sigma-Aldrich

Zirconium, powder, −100 mesh

Sigma-Aldrich

Zirkonium(IV)-oxid, 99.99% trace metals basis (purity excludes ~2% HfO₂)

Sigma-Aldrich

Zirconium, foil, thickness 0.1 mm, 99.98% trace metals basis

Sigma-Aldrich

Zirconium, rod, diam. 6.35 mm, ≥99% trace metals basis

Sigma-Aldrich

Zirconium, sponge, ≥99% trace metals basis

Sigma-Aldrich

Zirkonium(IV)-oxid -Lösung, nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H₂O

Sigma-Aldrich

Zirkonium(IV)-oxid -Lösung, nanoparticles, dispersion, <100 nm particle size (BET), 5 wt. % in H₂O

Zirkonium, foil, light tested, 150x150mm, thickness 0.05mm, annealed, 99.2%

Zirkonium, sponge, 500g, max. size 25mm, 99.2%

Zirkonium, rod, 100mm, diameter 1.5mm, 99.2%

Zirconium, rod, 500mm, diameter 1.5mm, 99.2%

Zirkonium, foil, 150x150mm, thickness 0.5mm, annealed, 99.2%

Zirkonium, rod, 1000mm, diameter 1.5mm, 99.2%

Zirkonium, foil, 25x25mm, thickness 2.0mm, annealed, 99.2%

Zirkonium, foil, light tested, 100x100mm, thickness 0.025mm, annealed, 99.2%

Zirconium, foil, 0.5m coil, thickness 0.5mm, annealed, 99.2%

Zirconium, foil, light tested, 25x25mm, thickness 0.05mm, annealed, 99.2%

Zirkonium, rod, 500mm, diameter 2.0mm, centerless ground, 99.2%

Zirconium, foil, light tested, 25x25mm, thickness 0.01mm, 99.2%

Zirkonium, rod, 100mm, diameter 2.0mm, centerless ground, 99.2%

Zirkonium, sponge, 100g, max. size 25mm, 99.2%

Zirkonium, tube, 100mm, outside diameter 1.6mm, inside diameter 1.1mm, wall thickness 0.25mm, hard, 99.2%

Zirkonium, foil, light tested, 25x25mm, thickness 0.02mm, 99.2%

Zirkonium, rod, 200mm, diameter 1.5mm, 99.2%

Zirkonium, sponge, 200g, max. size 25mm, 99.2%

Zirkonium, sponge, 50g, max. size 25mm, 99.2%

Zirkonium, foil, 50x50mm, thickness 0.5mm, annealed, 99.2%

Zirkonium, foil, 10mm disks, thickness 0.01mm, 99.2%