Metal doped nanosized titania used for the photocatalytic degradation of rhodamine B dye under visible-light.

Journal of nanoscience and nanotechnology (2013-08-02)
Mphilisi M Mahlambi, Ajay K Mishra, Shivani B Mishra, Rui W Krause, Bhekie B Mamba, Ashok M Raichur
PMID23901513
RESUMEN

Metal-doped anatase nanosized titania photocatalysts were successfully synthesized using a sol-gel process. Different amounts of the dopants (0.2, 0.4, 0.6, 0.8 and 1.0%) of the metals (Ag, Ni, Co and Pd) were utilized. The UV-Vis spectra (solid state diffuse reflectance spectra) of the doped nanoparticles exhibited a red shift in the absorption edge as a result of metal doping. The metal-doped nanoparticles were investigated for their photocatalytic activity under visible-light irradiation using Rhodamine B (Rh B) as a control pollutant. The results obtained indicate that the metal-doped titania had the highest activity at 0.4% metal loading. The kinetic models revealed that the photodegradation of Rh B followed a pseudo first order reaction. From ion chromatography (IC) analysis the degradation by-products Rhodamine B fragments were found to be acetate, chloride, nitrite, carbonate and nitrate ions.

MATERIALES
Referencia del producto
Marca
Descripción del producto
R6626
Sigma-Aldrich
Rhodamine B, ≥95% (HPLC)
718467
Sigma-Aldrich
Óxido de titanio (IV), nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis
637254
Sigma-Aldrich
Titanium(IV) oxide, anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis
14027
Sigma-Aldrich
Óxido de titanio (IV), puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%
83689
Sigma-Aldrich
Rhodamine B, for fluorescence
232033
Sigma-Aldrich
Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis
14021
Sigma-Aldrich
Óxido de titanio (IV), ReagentPlus®, ≥99%
224227
Sigma-Aldrich
Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis
248576
Sigma-Aldrich
Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis
637262
Sigma-Aldrich
Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis
634662
Sigma-Aldrich
Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis
348791
Sigma-Aldrich
Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis
366994
Sigma-Aldrich
Titanium, powder, <45 μm avg. part. size, 99.98% trace metals basis
267503
Sigma-Aldrich
Titanium, foil, thickness 0.25 mm, 99.7% trace metals basis
700347
Sigma-Aldrich
Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H2O, 99.5% trace metals basis
268496
Sigma-Aldrich
Titanium, powder, −100 mesh, 99.7% trace metals basis
204757
Sigma-Aldrich
Titanium(IV) oxide, rutile, ≥99.98% trace metals basis
204730
Sigma-Aldrich
Titanium(IV) oxide, rutile, 99.995% trace metals basis
677469
Sigma-Aldrich
Óxido de titanio (IV), contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%
268526
Sigma-Aldrich
Titanium, sponge, 1-20 mm, 99.5% trace metals basis
460400
Sigma-Aldrich
Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis
369489
Sigma-Aldrich
Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis
348848
Sigma-Aldrich
Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis
79754
Supelco
Rhodamine B, analytical standard
348805
Sigma-Aldrich
Titanium, foil, thickness 0.5 mm, 99.99% trace metals basis
767506
Sigma-Aldrich
Titanium, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis
460397
Sigma-Aldrich
Titanium, foil, thickness 0.127 mm, ≥99.99% trace metals basis
266035
Sigma-Aldrich
Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis
635057
Sigma-Aldrich
Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm
267481
Sigma-Aldrich
Titanium, foil, thickness 0.25 mm, 99.99% trace metals basis