FMLW04700
Alternativa più ecologica
Sinonimo/i:
Filtri a membrana Fluoropore
| Voi/SKU | Disponibilità | Prezzo |
|---|
PTFE membrane, gridded filter, white filter
non-sterile
hydrophobic
Fluoropore®, Millipore
Greener Alternative Product
0.82 L/min-cm2 air flow rate at 0.028 psi, 130 °C max. temp. (Curling may occur at elevated temperatures), 236 mL/min-cm2 liquid flow rate (27.5 in Hg (100% IPA))
47 mm
47 mm
254 μm , Typical
Fluoropore®
5.0 μm pore size, ≥60 % porosity
≥0.07 bar (0.97 psi), 100% IPA
ambient
1 of 1
Questo articolo | |||
|---|---|---|---|
| description Fluoropore®, filter diam. 47 mm, hydrophobic | description Fluoropore®, filter diam. 90 mm, hydrophobic | description Fluoropore®, filter diam. 47 mm, hydrophobic | description Fluoropore®, filter diam. 142 mm, hydrophobic |
| pore size ≥60 % porosity, 5.0 μm pore size | pore size 1.0 μm pore size, ≥65 % porosity | pore size >60 % porosity, 0.45 μm pore size | pore size 1.0 μm pore size, ≥65 % porosity |
| diam. 47 mm | diam. 90 mm | diam. 47 mm | diam. 142 mm |
| manufacturer/tradename Fluoropore®, Millipore | manufacturer/tradename Millipore, Fluoropore® | manufacturer/tradename Fluoropore®, Millipore | manufacturer/tradename Millipore, Fluoropore® |
| parameter 0.82 L/min-cm2 air flow rate at 0.028 psi, 130 °C max. temp. (Curling may occur at elevated temperatures), 236 mL/min-cm2 liquid flow rate (27.5 in Hg (100% IPA)) | parameter ≥150 mL/min-cm2 flow rate (27.5inHg, methanol), 130 °C max. temp. (Curling observed at elevated temperatures), ≥300 mL/min-cm2 air flow rate (Gurley) | parameter ≥60 mL/min-cm2 flow rate (27.5 inHg, methanol), >0.5 L/min-cm2 air flow rate (Gurley), 100 °C max. temp. (Curling may occur at elevated temperatures) | parameter ≥150 mL/min-cm2 flow rate (27.5 inHg, methanol), ≥300 mL/min-cm2 air flow rate (Gurley), 130 °C max. temp. (Curling observed at elevated temperatures) |
| material gridded filter, PTFE membrane, white filter | material white filter, plain filter, PTFE membrane | material white filter, plain filter, PTFE membrane | material plain filter, PTFE membrane, white filter |
| sterility non-sterile | sterility non-sterile | sterility non-sterile | sterility non-sterile |
Explore all of our products under Filtri a membrana PTFE con pori da 5,0 μm
10-13 - German Storage Class 10 to 13
Scegli una delle versioni più recenti:
I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.
What is the reason for the difference in air flow rate between the FSLW04700 Millipore Fluoropore with a 3.0 µm pore size and the FMLW04700 Millipore Fluoropore with a 5.0 µm pore size, both made of hydrophobic PTFE and 47 mm membrane?
The relationship between flow rate and pressure drop is such that the lower the flow rate, the lower the pressure drop. Fluoropore membranes come in 3 and 5 µm pore sizes. The smaller pore size offers low FWHM, while the larger pore size results in very low pressure drop and greater throughput capacity, thereby minimizing the number of filter changeouts.
*FWHM refers to the full width at half of the maximum height of the P0-218 peak obtained during sampling of room air.
Helpful?
Why is the backing of the FMLW04700 5.0 um PTFE 47mm disc gridded? Additionally, what is the reason for the gridded backing on FMLW03700, FMLW02500, SA1J014I14, and SA1J006I15, which are also "FMLW" discs with different diameters?
The FMLW04700 5 um PTFE membrane with a white gridded backing is designed for air alpha monitoring of radioactive particles. In this application, the filter membrane must be oriented in the alpha monitoring instrument so that the PTFE side faces the air flow. The gridded backing serves the purpose of making it easy to distinguish between the two sides. The backing is necessary because the PTFE membrane alone can be floppy and difficult to handle, particularly in field testing scenarios.
Helpful?