The thickness of the ITO layer is 300 nm. However, the surface roughness is not tested. Currently, there is no product available with a higher reported thickness.
Patterning service is not available.
917826
Indium tin oxide coated PEN
80% transparency, L × W × thickness 29.7 cm × 21 cm × 125 μm, sheet resistance <15 Ω/sq
Sinónimos:
ITO coated polyethylene naphthalate, ITO-PEN (80% transparency), PECF-IP
Iniciar sesiónpara Ver la Fijación de precios por contrato y de la organización
About This Item
Fórmula lineal:
In2O3 · (SnO2)x
Código UNSPSC:
12352303
NACRES:
NA.23
Productos recomendados
Materiales
substrate (Polyethylene naphthalate (PEN) film 125 micron thick (one side coated))
Nivel de calidad
resistencia de la lámina
<15 Ω/sq
L × An × grosor
29.7 cm × 21 cm × 125 μm
transmitancia
550 nm, 80%
Aplicación
This product is a one-side coated, highly transparent, flexible, ITO coated PEN polymer film. It is a ready-to-use flexible, transparent conducting substrate with low sheet resistance.
This product can be used for rapid fabrication of flexible electronics such as touch screen, Perovskite solar cells[1], sensors[2], and dye-sensitized solar cells[3].
This product can be used for rapid fabrication of flexible electronics such as touch screen, Perovskite solar cells[1], sensors[2], and dye-sensitized solar cells[3].
Palabra de señalización
Warning
Frases de peligro
Consejos de prudencia
Clasificaciones de peligro
STOT RE 2 Inhalation
Órganos de actuación
Lungs
Código de clase de almacenamiento
11 - Combustible Solids
Clase de riesgo para el agua (WGK)
WGK 3
Elija entre una de las versiones más recientes:
Certificados de análisis (COA)
Lot/Batch Number
¿No ve la versión correcta?
Si necesita una versión concreta, puede buscar un certificado específico por el número de lote.
¿Ya tiene este producto?
Encuentre la documentación para los productos que ha comprado recientemente en la Biblioteca de documentos.
Soumen Samanta et al.
Langmuir : the ACS journal of surfaces and colloids, 30(31), 9397-9406 (2014-07-17)
In this paper, we report a simple and versatile process of electrografting the aryl multilayers onto indium tin oxide (ITO)-coated flexible poly(ethylene naphthalate) (PEN) substrates using a diazonium salt (4-pyrrolylphenyldiazonium) solution, which was generated in situ from a reaction between
Photovoltaic Performance of Plastic Dye-Sensitized Electrodes Prepared by Low-Temperature Binder-Free Coating of Mesoscopic Titania.
Miyasaka T, et al.
Journal of the Electrochemical Society, 154(5) (2007)
Dependence of ITO-Coated Flexible Substrates in the Performance and Bending Durability of Perovskite Solar Cells.
Pandey M, et al.
Advanced Engineering Materials, 21(8), 1900288-1900288 (2019)
-
Good morning, What is the surface roughness and the thickness of the ITO on PEN substrates? Would it be possible to pattern the ITO? Do you have thicker ITO-coated PEN substrates?
1 answer-
Helpful?
-
Active Filters
Nuestro equipo de científicos tiene experiencia en todas las áreas de investigación: Ciencias de la vida, Ciencia de los materiales, Síntesis química, Cromatografía, Analítica y muchas otras.
Póngase en contacto con el Servicio técnico