923567
Nano Silver inkjet ink
photonically curable, low resistivity
Synonym(s):
Ag NP-based ink, Silver (Ag) Nanoparticle Ink, Silver nano ink, Smart′Ink S-CS01520, Electrodes, Silver-based Conductive ink
About This Item
Skip To
description
Electrodes
Quality Level
form
liquid
composition
alcohol / glycol mixture
concentration
20 wt. % Ag, 20 wt. %±1% (Silver content)
resistivity
5-10 μΩ-cm, after curing by photonic curing for less than 100ms, 3.2 - 6.3 Nb bulk silver, 5.4 μΩ-cm, after curing in furnace at 200° C for 5 minutes, 3.4 Nb bulk silver, 5.8 μΩ-cm, after curing in furnace at 180° C for 5 minutes, 3.6 Nb bulk silver, 6-12 μΩ-cm, after curing by NIR for a few seconds, 3.8 - 7.5 Nb bulk silver, 6.6 μΩ-cm, after curing in furnace at 150° C for 5 minutes, 4.1 Nb bulk silver
sheet resistance
13.5 m Ω/sq, 25 mum after curing at 200 Celsius for 5 min on glass, 16.5 m Ω/sq, 25 mum after curing at 150 Celsius for 5 min on glass
color
brown, Brown to Very Dark Brown and Faint Grey to Very Dark Grey and Black
surface tension
24 mN/m±3 mN/m
viscosity
12 mPa.s±3%(20 °C) (@100/s)
density
1.1 g/cm3
storage temp.
2-8°C
1 of 4
This Item | |||
|---|---|---|---|
| form liquid | form liquid | form suspension | form liquid |
| composition alcohol / glycol mixture (solvent) | composition - | composition Propylene glycol monomethyl ether - diethylene glycol monomethyl ether solvents (PM-DGME) (solvent), Silver content, 60 wt. % | composition - |
| concentration 20 wt. % Ag | concentration - | concentration - | concentration 50 wt. % |
| resistivity 5-10 μΩ-cm, after curing by photonic curing for less than 100ms, 3.2 - 6.3 Nb bulk silver | resistivity - | resistivity - | resistivity ≤20 μΩ-cm (after sintering at 200°C; 2h), ≤7 μΩ-cm (after sintering at 240°C; 4h) |
| sheet resistance 13.5 m Ω/sq, 25 mum after curing at 200 Celsius for 5 min on glass | sheet resistance - | sheet resistance - | sheet resistance - |
| color brown, Brown to Very Dark Brown and Faint Grey to Very Dark Grey and Black | color dark brown to blue | color - | color - |
Application
This ink has been developed to allow photonical curing to enable high throughput printing.
Compatible Printing Method: inkjet printing
Compatible Print heads: RICOH (MH5420), XAAR (1003 GS6, 128), KONIKA MINOLTA (KM512SHx, KM1024iMHE, KM1024LHB), FUJIFILM (Dimatix DMP series cartridge)
Compatible substrates: PET (Melinex 406, Melinex 339, Melines 520, Arcophane TCA, Arcophane STS, Folex BG-71), PEN (Teonex), Kapton® , Ceramic
Recommended surface treatment for substrates:
- Temperature stabilization
- Argon plasma treatment
Features and Benefits
- Improved conductivity
- Superior resolution (increased with substrate surface treatment)
- Good bending resistance, smooth surface
- Shiny coating, mirror effect
- Optimized nano-particle content
- Curing process compatibility: photonic, NIR, low vacuum oven, thermal curing
- Cleaning solution: C-FS21511
- Non-toxic (No CMR ink)
Legal Information
related product
signalword
Danger
hcodes
Hazard Classifications
Aquatic Acute 1 - Aquatic Chronic 1 - Eye Dam. 1 - Flam. Liq. 3 - Skin Irrit. 2
Storage Class
3 - Flammable liquids
wgk
WGK 3
flash_point_f
140.0 °F
flash_point_c
60 °C
Choose from one of the most recent versions:
Already Own This Product?
Find documentation for the products that you have recently purchased in the Document Library.
Global Trade Item Number
| SKU | GTIN |
|---|---|
| 923567-25ML | 04065267169415 |
Active Filters
Our team of scientists has experience in all areas of research including Life Science, Material Science, Chemical Synthesis, Chromatography, Analytical and many others.
Contact Technical Service