InVO4/TiO2 composite for visible-light photocatalytic degradation of 2-chlorophenol in wastewater.

InVO4/TiO2 composite for visible-light photocatalytic degradation of 2-chlorophenol in wastewater.

Environmental technology (2014-08-26)

J Rashid, M A Barakat, S L Pettit, J N Kuhn

ABSTRACT

InVO4/TiO2 composite was synthesized via amalgamation of InVO4 with TiO2 (Degussa P-25) powders. Application of the produced composite was evaluated as a catalyst for visible-light photocatalytic degradation of 2-chlorophenol (2-CP) in synthetic wastewater solutions. The catalyst was characterized by X-ray diffraction (XRD), scanning electron microscopy energy dispersive X-ray microanalyses and nitrogen physisorption. The degradation of 2-CP was affected by solution pH, light intensity, photocatalyst dosage and 2-CP initial concentration. InVO4/TiO2 showed higher photocatalytic degradation of 2-CP as compared with Degussa P-25 TiO2. Complete degradation of 2-CP was achieved with the InVO4/TiO2 catalyst under optimized conditions (1 g/L catalyst with a pollutant concentration of 50 mg/L at solution pH 5 and irradiation time of 180 min). Comparatively, 2-CP degradation efficiency of 50.5% was achieved with the TiO2 (Degussa P-25) at the same experimental conditions. The study confirmed that InVO4/TiO2 has high potential for degradation of 2-CP from wastewater under visible-light irradiation.

MATERIALS

Product Number

Brand

Product Description

GF35446316

Titanium, rod, 100mm, diameter 20mm, annealed, 99.6+%

GF21200746

Titanium, tube, 100mm, outside diameter 0.81mm, inside diameter 0.61mm, wall thickness 0.1mm, as drawn, 99.6+%

GF99390134

Titanium, rod, 100mm, diameter 3.0mm, annealed, 99.6+%

GF73866998

Titanium, tube, 100mm, outside diameter 12.7mm, inside diameter 10.9mm, wall thickness 0.9mm, annealed, 99.6+%

GF39390880

Titanium, tube, 200mm, outside diameter 6.35mm, inside diameter 4.57mm, wall thickness 0.89mm, annealed, 99.6+%

GF29374005

Titanium, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

GF35682600

Titanium, tube, 200mm, outside diameter 6.1mm, inside diameter 5.1mm, wall thickness 0.5mm, annealed, 99.6+%

GF83238127

Titanium, tube, 100mm, outside diameter 3.0mm, inside diameter 1.5mm, wall thickness 0.75mm, annealed, 99.6+%

GF73915128

Titanium, tube, 100mm, outside diameter 6.35mm, inside diameter 4.57mm, wall thickness 0.89mm, annealed, 99.6+%

GF82391878

Titanium, rod, 50mm, diameter 8.0mm, as drawn, 99.99+%

GF33373795

Titanium, tube, 200mm, outside diameter 12.7mm, inside diameter 10.9mm, wall thickness 0.9mm, annealed, 99.6+%

GF35130035

Titanium, rod, 25mm, diameter 9.5mm, annealed, 99.99+%

GF63527003

Titanium, tube, 200mm, outside diameter 9.5mm, inside diameter 8.2mm, wall thickness 0.65mm, annealed, 99.6+%

GF17395375

Titanium, tube, 1000mm, outside diameter 2.03mm, inside diameter 1.63mm, wall thickness 0.2mm, annealed, 99.6+%

268496

Sigma-Aldrich

Titanium, powder, −100 mesh, 99.7% trace metals basis

268526

Sigma-Aldrich

Titanium, sponge, 1-20 mm, 99.5% trace metals basis

718467

Sigma-Aldrich

Titanium(IV) oxide, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

433667

Sigma-Aldrich

Titanium, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

C62794

Sigma-Aldrich

2-Chlorophenol, 98%

267503

Sigma-Aldrich

Titanium, foil, thickness 0.25 mm, 99.7% trace metals basis

460397

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, ≥99.99% trace metals basis

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

348805

Sigma-Aldrich

Titanium, foil, thickness 0.5 mm, 99.99% trace metals basis

185779

Sigma-Aldrich

2-Chlorophenol, ≥99%

677469

Sigma-Aldrich

Titanium(IV) oxide, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

36746

Supelco

2-Chlorophenol, PESTANAL^®, analytical standard

IRMM531A

Titanium, IRMM^®, certified reference material, 0.1 mm foil

348864

Sigma-Aldrich

Titanium, wire, diam. 0.5 mm, 99.99% trace metals basis

366994

Sigma-Aldrich

Titanium, powder, <45 μm avg. part. size, 99.98% trace metals basis

267481

Sigma-Aldrich

Titanium, foil, thickness 0.25 mm, 99.99% trace metals basis