Effect of TiO2 on the photocatalytic properties of bismuth oxide.

Effect of TiO2 on the photocatalytic properties of bismuth oxide.

Environmental technology (2014-04-08)

Gourav Singla, K Singh

PMID24701951

ABSTRACT

Bi2-xTixO3+x/2 (x = 0.05, 0.10 and 0.15) photocatalysts are prepared by solid-state technique. The band gap of the prepared sample was estimated from the onset of UV-Vis absorption spectra. The photocatalytic activities of as prepared samples are investigated under UV light irradiation for the decomposition of methyl orange (MO). It has been observed that the rate of decomposition of MO increased with increasing Ti4+ content in the present samples. Moreover, it shows better photocatalytic activity than undoped Bi2O3 and TiO2. The lowest band gap is observed for x = 0.15 sample, i.e. 2.55 eV, which also showed the highest photocatalytic activity in the present sample.

MATERIALS

Product Number

Brand

Product Description

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

700355

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticle, <250 nm particle size (DLS), paste, 53-57 wt. % in diethylene glycol monobutyl ether/ethylene glycol, 99.9% trace metals basis

700339

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <100 nm particle size, dispersion, 48-52 wt. % in xylene, 99.9% trace metals basis

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

635065

Sigma-Aldrich

Titanium(IV) oxide, rutile, <110>, single crystal substrate, ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

68250

Sigma-Aldrich

Methyl Orange, for microscopy (Hist.), indicator (pH 3.0-4.4)

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

114510

Sigma-Aldrich

Methyl Orange, ACS reagent, Dye content 85 %

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

14027

Sigma-Aldrich

Titanium(IV) oxide, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

14021

Sigma-Aldrich

Titanium(IV) oxide, ReagentPlus^®, ≥99%

GF05789425

Bismuth, foil, not light tested, 25x25mm, thickness 0.025mm, permanent polyester support, 99.97%

718467

Sigma-Aldrich

Titanium(IV) oxide, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

677469

Sigma-Aldrich

Titanium(IV) oxide, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

265462

Sigma-Aldrich

Bismuth, powder, −100 mesh, 99% trace metals basis

232033

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis

264008

Sigma-Aldrich

Bismuth, powder, −100 mesh, ≥99.99% trace metals basis

265470

Sigma-Aldrich

Bismuth, shot, 4-30 mesh, 99.9% trace metals basis

452386

Sigma-Aldrich

Bismuth, beads, 1-5 mm, 99.999% trace metals basis

95372

Sigma-Aldrich

Bismuth, granular, ≥99.99% trace metals basis

556130

Sigma-Aldrich

Bismuth, pieces, 1-12 mm, 99.999% trace metals basis

223891

Sigma-Aldrich

Bismuth(III) oxide, ReagentPlus^®, powder, 10 μm, 99.9% trace metals basis

202827

Sigma-Aldrich

Bismuth(III) oxide, powder, 99.999% trace metals basis

774510

Sigma-Aldrich

Titanium(IV) oxide, nanowires, diam. × L ~100 nm × 10 μm

774529

Sigma-Aldrich

Titanium(IV) oxide, nanowires, diam. × L ~10 nm × 10 μm

637017

Sigma-Aldrich

Bismuth(III) oxide, nanopowder, 90-210 nm particle size, 99.8% trace metals basis