Halloysite Nanotubes Applications in Nanomaterials Research

Prof. Yuri Lvov, Dr. Ronald Price

Institute for Micromanufacturing, Louisiana Tech University, Ruston, LA 71272

Halloysite, a naturally occurring aluminosilicate nanotube, has been undeservedly forgotten. Halloysite (Al₂Si₂O₅(OH)₄•2H₂O) is a two-layered aluminosilicate, with a predominantly hollow tubular structure in the submicron range and chemically similar to kaolin^1,2. The neighboring alumina and silica layers, and their waters of hydration, curve and form multilayer tubes (Figure 1) due to a packing disorder. Halloysite is an economically viable material that can be mined from the corresponding deposit as a raw mineral.² As for most natural materials, the size of halloysite particles varies within 1-15 microns of length and 10-150 nm of inner diameter, depending on the deposits. In our research, we use halloysite G produced by Applied Minerals, Inc. and available (Cat. No. 685445). This material has an average tube diameter of 50 nm and inner lumen diameter of 15 nm (Figure 1). Typical specific surface area of this halloysite is 65 m²/g; pore volume of ~ 1.25 mL/g; refractive index 1.54; and specific gravity 2.53 g/cm^3.

Figure 1. TEM Image of 50 nm diameter halloysite nanotubules 685445 (a) and tube cross-section (b).

Chemically, the outer surface of the halloysite nanotubes has properties similar to SiO₂ while the inner cylinder core is related to Al₂O₃. The charge (zeta potential) behavior of halloysite particles can be roughly described by superposition of mostly negative (at pH 6-7) surface potential of SiO₂, with a small contribution from the positive Al₂O₃ inner surface.^3,4 The positive (below pH 8.5) charge of the inner lumen promotes loading of halloysite nanotubes with negative macromolecules, which are at the same time repelled from the negatively charged outer surfaces. A wide range of active agents, including drugs,^5-9 nicotinamide adenine dineculeotide (NAD), and marine biocides,⁹ can be entrapped within the inner lumen, as well as within void spaces of the multilayered aluminosilicate shells. This entrapment can be followed by retention and release of the agents, making the halloysite a nanomaterial well suited for macromolecular delivery applications.

We studied loading and release of macromolecules from the halloysite nanotubules. Loading was performed as follows: A vial containing the mixture of halloysite and saturated solution of targeted molecules was transferred to a vacuum jar and then repeatedly evacuated using a vacuum pump. Slight fizzing of the suspension indicates the air being removed from the halloysite interior. After the fizzing stopped, the vial was sealed for 30 minutes to reach equilibrium in molecule distribution. The halloysite suspension was centrifuged to remove excess dissolved molecules and washed. The process may be repeated twice to ensure that the halloysite is filled with the maximum amount of the targeted molecules. With this simple loading technique, one can fill nanotubule lumen with any materials, such as drugs, proteins, polyelectrolytes, and nanoparticles of proper diameter using old-fashioned method similar to muzzle loading with bullets.

Both hydrophobic and hydrophilic agents can be entrapped after an appropriate pre-treatment of the halloysite surface.^10-11 For example, we recently demonstrated loading of the halloysite with urease for bio-catalytic CaCO₃ synthesis in the tubule lumen.¹¹ For hydrophilic molecules (like kellin, NAD, tetracycline) a typical release time was 2-5 hours and for molecules with low solubility in water (like dexamethasone, furosemide, nifedipine) release time 5-20 hours was observed (Figure 2). Macromolecular release profiles from the halloysite are well described by a one-dimensional diffusion model through the nanotube lumen opening.

Figure 2. Release of macromolecules from halloysite nanotubules (NAD, dexamethasone, furosemide, nifedipine). Steep curves show direct dissolution of the molecule microcrystals without tubule loading.

We foresee a great deal of fundamental research and many applications employing halloysite clay nanotubules. Research will include:

• Control of loading and release of macromolecules by making stoppers or narrowing the exits from the nanotubule lumen
• Development of the tubule nanoreactor concept by carrying out reactions at the openings of the halloysite nanotubules between loaded molecules and molecules in bulk solution

Possible applications of halloysite nanotubes include:

• Controlled release of anticorrosion agents
• Sustained release of herbicides, insecticides, fungicides and anti-microbials
• Sustained release of drugs, food additives, and fragrances
• Templating synthesis of rod-like nanoparticles
• Uses as catalytic supports and molecular sieves
• Specific ion adsorption
• Use as plastic fillers for strength reinforcement and scratch protection
• Use in advanced ceramic materials, especially biocompatible implants.

1. Joussein E, Petit S, Churchman J, Theng B, Righi D, Delvaux B. 2005. Halloysite clay minerals ? a review. Clay miner.. 40(4):383-426. https://doi.org/10.1180/0009855054040180

2. Hope EW, Kittrick JA. 1964. Surface tension and the morphology of halloysite. Am. Mineral. 49(7):859-63.

3. Tar?? G, Bobos I, Gomes CS, Ferreira JM. 1999. Modification of Surface Charge Properties during Kaolinite to Halloysite-7Å Transformation. Journal of Colloid and Interface Science. 210(2):360-366. https://doi.org/10.1006/jcis.1998.5917

4. Baral S, Brandow S, Gaber BP. 1993. Electroless metalization of halloysite, a hollow cylindrical 1:1 aluminosilicate of submicron diameter. Chem. Mater.. 5(9):1227-1232. https://doi.org/10.1021/cm00033a008

5. Levis S, Deasy P. 2003. Use of coated microtubular halloysite for the sustained release of diltiazem hydrochloride and propranolol hydrochloride. International Journal of Pharmaceutics. 253(1-2):145-157. https://doi.org/10.1016/s0378-5173(02)00702-0

6. 2001. Contributed Papers in Specimen Mineralogy: 27th Rochester Mineralogical Symposium. Rocks & Minerals. 76(4):252-258. https://doi.org/10.1080/00357520109603226

7. Yang L, Fassihi R. 1997. Examination of drug solubility, polymer types, hydrodynamics and loading dose on drug release behavior from a triple-layer asymmetric configuration delivery system. International Journal of Pharmaceutics. 155(2):219-229. https://doi.org/10.1016/s0378-5173(97)00164-6

8. Lvov Y, Price R, Gaber B, Ichinose I. 2002. Thin film nanofabrication via layer-by-layer adsorption of tubule halloysite, spherical silica, proteins and polycations. Colloids and Surfaces A: Physicochemical and Engineering Aspects. 198-200375-382. https://doi.org/10.1016/s0927-7757(01)00970-0

9. R. Price, B. P. Gaber, Y. Lvov R. 2001. In-vitro release characteristics of tetracycline HCl, khellin and nicotinamide adenine dineculeotide from halloysite; a cylindrical mineral. Journal of Microencapsulation. 18(6):713-722. https://doi.org/10.1080/02652040010019532

10. Lvov YM, Shchukin DG, Möhwald H, Price RR. 2008. Halloysite Clay Nanotubes for Controlled Release of Protective Agents. ACS Nano. 2(5):814-820. https://doi.org/10.1021/nn800259q

11. Shchukin D, Sukhorukov G, Price R, Lvov Y. 2005. Halloysite Nanotubes as Biomimetic Nanoreactors. Small. 1(5):510-513. https://doi.org/10.1002/smll.200400120