Surface enhanced fluorescence from silver film substrate decorated with nanohole arrays.

Surface enhanced fluorescence from silver film substrate decorated with nanohole arrays.

Journal of nanoscience and nanotechnology (2014-04-18)

Yu Sun, Xiao Qing Yan, Yabing Du, Zhenglong Zhang, Yiping Huo, Fei Gao, Hairong Zheng

ABSTRACT

The fluorescence enhancement effect of Rh6G molecules deposited on the silver film substrate decorated with nanohole arrays was investigated in this paper. The prepared substrate, decorated with nanohole arrays, was fabricated with the deposition of silver films onto the anodic aluminum oxide templates through magnetron sputtering method. Compared with the conventional continuous silver film substrate, the prepared substrate shows better enhanced effect. Particularly, the fluorescence enhancement factor has a relationship with the size and period of the nanohole arrays. The experimental observations were analyzed with local surface plasmon resonance model. The results of current work highlight the importance of strong electromagnetic coupling effect in surface enhanced fluorescence.

MATERIALS

Product Number

Brand

Product Description

Sigma-Aldrich

Silver, wire, diam. 0.25 mm, ≥99.99% trace metals basis

Sigma-Aldrich

Silver, powder, 5-8 μm, ≥99.9% trace metals basis

Sigma-Aldrich

Silver, foil, thickness 0.025 mm, 99.9% trace metals basis

Sigma-Aldrich

Silver, powder, 2-3.5 μm, ≥99.9% trace metals basis

Sigma-Aldrich

Silver, foil, thickness 0.25 mm, 99.9% trace metals basis

Sigma-Aldrich

Silver, wire, diam. 2.0 mm, 99.9% trace metals basis

Sigma-Aldrich

Silver, wire, diam. 2.0 mm, ≥99.99% trace metals basis

Sigma-Aldrich

Silver, granular, >250 μm, 99.99% trace metals basis

Sigma-Aldrich

Silver, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis

Sigma-Aldrich

Silver, wire, diam. 0.5 mm, 99.9% trace metals basis

Sigma-Aldrich

Silver, flakes, 10 μm, ≥99.9% trace metals basis

Sigma-Aldrich

Silver, powder, <45 μm, ≥99.99% trace metals basis

Sigma-Aldrich

Silver, wire, diam. 1.5 mm, ≥99.99% trace metals basis

Sigma-Aldrich

Silver, nanopowder, <100 nm particle size, contains PVP as dispersant, 99.5% trace metals basis

Sigma-Aldrich

Silver, wire, diam. 0.25 mm, 99.9% trace metals basis

Silver, foil, 0.5m coil, thickness 0.1mm, annealed, 99.95+%

Silver, foil, 10mm disks, thickness 0.125mm, as rolled, 99.95+%

Silver, foil, 10mm disks, thickness 0.1mm, annealed, 99.95+%

Silver, foil, light tested, 25x25mm, thickness 0.025mm, annealed, 99.95+%

Silver, foil, not light tested, 25x25mm, thickness 0.001mm, 99.97%

Silver, foil, 6mm disks, thickness 0.009mm, 99.97%

Silver, foil, 6mm disks, thickness 0.003mm, 99.9%

Silver, foil, 6mm disks, thickness 0.0125mm, 99.95+%

Silver, foil, 6mm disks, thickness 0.01mm, 99.95+%

Silver, foil, 6mm disks, thickness 0.007mm, 99.97%

Silver, foil, 6mm disks, thickness 0.25mm, as rolled, 99.95+%

Silver, foil, 8mm disks, thickness 0.006mm, 99.97%

Silver, foil, not light tested, 25x25mm, thickness 0.007mm, 99.97%

Silver, foil, 8mm disks, thickness 0.02mm, 99.97%

Silver, foil, 6mm disks, thickness 0.25mm, as rolled, 99.99+%