Sorptive extraction using polydimethylsiloxane/metal-organic framework coated stir bars coupled with high performance liquid chromatography-fluorescence detection for the determination of polycyclic aromatic hydrocarbons in environmental water samples.

Sorptive extraction using polydimethylsiloxane/metal-organic framework coated stir bars coupled with high performance liquid chromatography-fluorescence detection for the determination of polycyclic aromatic hydrocarbons in environmental water samples.

Journal of chromatography. A (2014-07-09)

Cong Hu, Man He, Beibei Chen, Cheng Zhong, Bin Hu

ABSTRACT

In this work, metal-organic frameworks (MOFs, Al-MIL-53-NH₂) were synthesized via the hydrothermal method, and novel polydimethylsiloxane/metal-organic framework (PDMS/MOFs, PDMS/Al-MIL-53-NH₂)-coated stir bars were prepared by the sol-gel technique. The preparation reproducibility of the PDMS/MOFs-coated stir bar was good, with relative standard deviations (RSDs) ranging from 4.8% to 14.9% (n=7) within one batch and from 6.2% to 16.9% (n=6) among different batches. Based on this fact, a new method of PDMS/MOFs-coated stir bar sorptive extraction (SBSE) and ultrasonic-assisted liquid desorption (UALD) coupled with high performance liquid chromatography-fluorescence detection (HPLC-FLD) was developed for the determination of polycyclic aromatic hydrocarbons (PAHs) in environmental water samples. To obtain the best extraction performance for PAHs, several parameters affecting SBSE, such as extraction time, stirring rate, and extraction temperature, were investigated. Under optimal experimental conditions, wide linear ranges and good RSDs (n=7) were obtained. With enrichment factors (EFs) of 16.1- to 88.9-fold (theoretical EF, 142-fold), the limits of detection (LODs, S/N=3) of the developed method for the target PAHs were found to be in the range of 0.05-2.94 ng/L. The developed method was successfully applied to the analysis of PAHs in Yangtze River and East Lake water samples.

MATERIALS

Product Number

Brand

Product Description

11009

Sigma-Aldrich

Aluminum, powder, ≥91% (complexometric)

IRMM523B

Aluminum, IRMM^®, certified reference material, 1.0 mm foil

433705

Sigma-Aldrich

Aluminum, evaporation slug, diam. × L 6.3 mm × 6.3 mm, 99.999% trace metals basis

326887

Sigma-Aldrich

Aluminum, wire, diam. 0.58 mm, ≥99.99% trace metals basis

326941

Sigma-Aldrich

Aluminum, pellets, 3-8 mesh, ≥99.999% trace metals basis

266558

Sigma-Aldrich

Aluminum, wire, diam. 1.0 mm, 99.999% trace metals basis

518573

Sigma-Aldrich

Aluminum, granular, <1 mm, 99.7% trace metals basis

IRMM523C

Aluminum, IRMM^®, certified reference material, 1.0 mm wire

733369

Sigma-Aldrich

Aluminum, foil, thickness 8 μm, 99% trace metals basis

GF72634103

Aluminum, rod, 50mm, diameter 28mm, as drawn, 99.999%

GF48798309

Aluminum, rod, 100mm, diameter 6.0mm, as drawn, 99.999%

GF72881297

Aluminum, microfoil, disks, 50mm, thinness 1.0μm, specific density 269.9μg/cm², permanent mylar 3.5μm support, 99.999%

GF98025239

Aluminum, tube, 100mm, outside diameter 0.55mm, inside diameter 0.4mm, wall thickness 0.075mm, as drawn, 99.5%

GF04709695

Aluminum, rod, 44mm, diameter 77.5mm, as drawn, 99.999%

GF02208923

Aluminum, tube, 200mm, outside diameter 0.86mm, inside diameter 0.76mm, wall thickness 0.05mm, as drawn, 99.5%

GF09680306

Aluminum, microfoil, disks, 25mm, thinness 0.0075μm, specific density 1.84μg/cm², permanent mylar 3.5μm support, 99.999%

GF87559420

Aluminum, tube, 0.5m coil, as drawn, outside diameter 0.30mm, inside diameter 0.2mm, wall thickness 0.05mm, 99.5%

GF09755837

Aluminum, wire reel, 100m, diameter 0.5mm, as drawn, 99.95+%

GF71298546

Aluminum, wire reel, 100m, diameter 0.063mm, annealed, 99.99%

GF49694743

Aluminum, tube, 100mm, outside diameter 0.6mm, inside diameter 0.3mm, wall thickness 0.15mm, as drawn, 99.5%

GF94706354

Aluminum, mesh, 150x150mm, nominal aperture 0.38mm, wire diameter 0.25mm, 40x40 wires/inch, open area 37%, plain weave mesh

GF93309037

Aluminum, tube, 200mm, outside diameter 1.42mm, inside diameter 1.166mm, wall thickness 0.127mm, as drawn, 99.5%

GF06197014

Aluminum, rod, 200mm, diameter 10.0mm, as drawn, 99.999%

GF54273944

Aluminum, tube, 500mm, outside diameter 0.55mm, inside diameter 0.4mm, wall thickness 0.075mm, as drawn, 99.5%

GF16562246

Aluminum, tube, 500mm, outside diameter 3.0mm, inside diameter 1.62mm, wall thickness 0.69mm, hard, 99.5%

GF95990068

Aluminum, wire reel, 100m, diameter 0.25mm, hard, 99.99+%

GF98718935

Aluminum, sphere, 100pcs, diameter 1.0mm, aluminum alloy 2017 precision sphere, grade 200, 95.2%

GF51598761

Aluminum, rod, 200mm, diameter 12.7mm, 99%

GF06074120

Aluminum, wire reel, 0.5m, diameter 1.0mm, as drawn, 99.999%

GF93280732

Aluminum, rod, 500mm, diameter 15.0mm, as drawn, 99.999%