Engineering bamboo-type TiO2 nanotube arrays to enhance their photocatalytic property.

Engineering bamboo-type TiO2 nanotube arrays to enhance their photocatalytic property.

Journal of nanoscience and nanotechnology (2014-04-18)

Dongsheng Guan, Paul J Hymel, Chengjun Zhou, Ying Wang

ABSTRACT

Bamboo-type TiO2 nanotube arrays with high surface area can be synthesized by alternating voltage (AV) anodization for their important use as photocatalytic medium. Their morphologies are highly dependent on preparation parameters including anodization time and electrolyte composition. Minimum time of high-voltage steps required for forming desired bamboo ridge spacing on these nanotubes can be calculated from current-time profiles recorded during potentiostatic anodization at the voltage. Water content in NH4F-containing ethylene glycol (EG) electrolytes is optimized simply from analyses of current transients or current-voltage relations for anodization in EG electrolytes with different amount of water, in order to achieve efficient electrochemical growth of TiO2 nanotubes for large ridge density and long tube length. Two types of bamboo-type TiO2 nanotubes with the same length of 5.46 microm but different ridge spacing are synthesized for photocatalytic degradation of methylene blue (MB) under UV radiation. Both of the bamboo-type nanotube arrays show improved photo catalysis compared to smooth TiO2 nanotubes of the same length, due to their larger surface area favorable for heterogeneous catalytic processes. In particular, the apparent rate constant of photocatalytic degradation on bamboo-type nanotubes is up to 29.4% higher than that for degradation on smooth ones.

MATERIALS

Product Number

Brand

Product Description

718467

Sigma-Aldrich

Titanium(IV) oxide, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

77515

Sigma-Aldrich

Methylene Blue solution, for microscopy

50484

Sigma-Aldrich

Methylene Blue solution, suitable for microbiology

268496

Sigma-Aldrich

Titanium, powder, −100 mesh, 99.7% trace metals basis

268526

Sigma-Aldrich

Titanium, sponge, 1-20 mm, 99.5% trace metals basis

433667

Sigma-Aldrich

Titanium, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

IRMM531A

Titanium, IRMM^®, certified reference material, 0.1 mm foil

03978

Sigma-Aldrich

Methylene Blue solution, for microscopy, concentrate according to Ehrlich, concentrated, aqueous solution

677469

Sigma-Aldrich

Titanium(IV) oxide, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

348864

Sigma-Aldrich

Titanium, wire, diam. 0.5 mm, 99.99% trace metals basis

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

348805

Sigma-Aldrich

Titanium, foil, thickness 0.5 mm, 99.99% trace metals basis

366994

Sigma-Aldrich

Titanium, powder, <45 μm avg. part. size, 99.98% trace metals basis

267481

Sigma-Aldrich

Titanium, foil, thickness 0.25 mm, 99.99% trace metals basis

232033

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis

267503

Sigma-Aldrich

Titanium, foil, thickness 0.25 mm, 99.7% trace metals basis

460397

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, ≥99.99% trace metals basis

774510

Sigma-Aldrich

Titanium(IV) oxide, nanowires, diam. × L ~100 nm × 10 μm

637254

Sigma-Aldrich

Titanium(IV) oxide, anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis

14021

Sigma-Aldrich

Titanium(IV) oxide, ReagentPlus^®, ≥99%

GF35683218

Titanium, microfoil, disks, 25mm, thinness 1.0μm, specific density 429μg/cm², permanent mylar 3.5μm support, 99.6+%

GF99390134

Titanium, rod, 100mm, diameter 3.0mm, annealed, 99.6+%

GF96834493

Titanium, rod, 1000mm, diameter 5mm, annealed, 99.6+%

GF21200746

Titanium, tube, 100mm, outside diameter 0.81mm, inside diameter 0.61mm, wall thickness 0.1mm, as drawn, 99.6+%

GF39390880

Titanium, tube, 200mm, outside diameter 6.35mm, inside diameter 4.57mm, wall thickness 0.89mm, annealed, 99.6+%

GF45586985

Titanium, rod, 200mm, diameter 1.5mm, annealed, 99.6+%

GF17395375

Titanium, tube, 1000mm, outside diameter 2.03mm, inside diameter 1.63mm, wall thickness 0.2mm, annealed, 99.6+%

GF57414179

Titanium, rod, 1000mm, diameter 6mm, annealed, 99.6+%

GF14423633

Titanium, rod, 1000mm, diameter 4mm, annealed, 99.6+%

GF29374005

Titanium, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh