Surface enhanced fluorescence from silver film substrate decorated with nanohole arrays.

Journal of nanoscience and nanotechnology (2014-04-18)
Yu Sun, Xiao Qing Yan, Yabing Du, Zhenglong Zhang, Yiping Huo, Fei Gao, Hairong Zheng
ABSTRACT

The fluorescence enhancement effect of Rh6G molecules deposited on the silver film substrate decorated with nanohole arrays was investigated in this paper. The prepared substrate, decorated with nanohole arrays, was fabricated with the deposition of silver films onto the anodic aluminum oxide templates through magnetron sputtering method. Compared with the conventional continuous silver film substrate, the prepared substrate shows better enhanced effect. Particularly, the fluorescence enhancement factor has a relationship with the size and period of the nanohole arrays. The experimental observations were analyzed with local surface plasmon resonance model. The results of current work highlight the importance of strong electromagnetic coupling effect in surface enhanced fluorescence.

MATERIALS
Product Number
Brand
Product Description

Sigma-Aldrich
Silver, wire, diam. 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
Silver, flakes, 10 μm, ≥99.9% trace metals basis
Sigma-Aldrich
Silver, powder, 2-3.5 μm, ≥99.9% trace metals basis
Sigma-Aldrich
Silver, wire, diam. 1.5 mm, ≥99.99% trace metals basis
Sigma-Aldrich
Silver, wire, diam. 0.25 mm, ≥99.99% trace metals basis
Sigma-Aldrich
Silver, powder, 5-8 μm, ≥99.9% trace metals basis
Sigma-Aldrich
Silver, wire, diam. 2.0 mm, ≥99.99% trace metals basis
Sigma-Aldrich
Silver, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis
Sigma-Aldrich
Silver, granular, >250 μm, 99.99% trace metals basis
Sigma-Aldrich
Silver, powder, <45 μm, ≥99.99% trace metals basis
Sigma-Aldrich
Silver, wire, diam. 0.5 mm, 99.9% trace metals basis
Sigma-Aldrich
Silver, foil, thickness 0.025 mm, 99.9% trace metals basis
Sigma-Aldrich
Silver, foil, thickness 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
Silver, wire, diam. 2.0 mm, 99.9% trace metals basis
Sigma-Aldrich
Silver, nanopowder, <100 nm particle size, contains PVP as dispersant, 99.5% trace metals basis
Silver, foil, 25x25mm, thickness 0.25mm, as rolled, 99.99+%
Silver, foil, 50x50mm, thickness 0.15mm, as rolled, 99.95+%
Silver, foil, 10mm disks, thickness 0.0025mm, 99.97%
Silver, foil, not light tested, 25x25mm, thickness 0.008mm, 99.97%
Silver, tube, 1000mm, outside diameter 6.0mm, inside diameter 4mm, wall thickness 1.0mm, as drawn, 99.95+%
Silver, insulated wire, 5m, conductor diameter 0.075mm, insulation thickness 0.010mm, nylon insulation, 99.99%
Silver, tube, 1000mm, outside diameter 0.7mm, inside diameter 0.3mm, wall thickness 0.2mm, as drawn, 99.95+%
Silver, insulated wire, 50m, conductor diameter 0.125mm, insulation thickness 0.0125mm, polyester insulation, 99.99%
Silver, rod, 50mm, diameter 12.7mm, as drawn, 99.95+%
Silver, insulated wire, 20m, conductor diameter 0.25mm, insulation thickness 0.023mm, polyester insulation, 99.99%
Silver, tube, 100mm, outside diameter 6.0mm, inside diameter 4mm, wall thickness 1.0mm, as drawn, 99.95+%
Silver, rod, 100mm, diameter 3.0mm, as drawn, 99.997%
Silver, foil, not light tested, 50x50mm, thickness 0.025mm, as rolled, 99.95+%
Silver, microfoil, disks, 10mm, thinness 0.5μm, specific density 522.6μg/cm2, permanent mylar 3.5μm support, 99.95+%
Silver, rod, 100mm, diameter 1.0mm, as drawn, 99.95+%