Synthesis and characterization of CoFe2O4/polyaniline nanocomposites for electromagnetic interference applications.

Synthesis and characterization of CoFe2O4/polyaniline nanocomposites for electromagnetic interference applications.

Journal of nanoscience and nanotechnology (2014-04-18)

K Praveena, S Srinath

RÉSUMÉ

The Cobalt ferrite (CoFe2O4) powders were synthesized by Co-precipitation method. The as prepared ferrite powders were incorporated into a polyaniline matrix at various volumetric ratios. The as prepared composites of ferrite and polyaniline powders were characterized using X-ray diffraction (XRD), transmission electron microscope (TEM). The particle size of CoFe2O4 is found to be 20 nm. The saturation magnetization (M(s)) of all the composites was found to be decreasing with decrease of ferrite content, while coercivity (H(c)) remained at the value corresponding to pure cobalt ferrite nanopowders. The complex permittivity (epsilon' and epsilon") and permeability (mu' and mu") of composite samples were measured in the range of 1 MHz to 1.1 GHz. The value of epsilon' and mu' found to be increased with ferrite volume concentration.

MATÉRIAUX

Référence du produit

Marque

Description du produit

310050

Sigma-Aldrich

Iron(III) oxide, powder, <5 μm, ≥96%

544884

Sigma-Aldrich

Iron(III) oxide, nanopowder, <50 nm particle size (BET)

529311

Sigma-Aldrich

Iron(III) oxide, ≥99.995% trace metals basis

266639

Sigma-Aldrich

Cobalt, powder, 2 μm particle size, 99.8% trace metals basis

266647

Sigma-Aldrich

Cobalt, powder, <150 μm, ≥99.9% trace metals basis

203076

Sigma-Aldrich

Cobalt, granular, 99.99% trace metals basis

697745

Sigma-Aldrich

Cobalt, Carbon coated magnetic, nanopowder, <50 nm particle size (TEM), ≥99%

266655

Sigma-Aldrich

Cobalt, pieces, 99.5% trace metals basis

356867

Sigma-Aldrich

Cobalt, foil, thickness 0.1 mm, 99.95% trace metals basis

398810

Sigma-Aldrich

Cobalt, rod, diam. 5.0 mm, 99.95% trace metals basis

266701

Sigma-Aldrich

Cobalt, wire, diam. 1.0 mm, 99.995% trace metals basis

GF76259593

Cobalt, foil, 100x100mm, thickness 2.0mm, as rolled, 99.9%

GF56494187

Cobalt, foil, 100x100mm, thickness 1.0mm, as rolled, 99.9%

356891

Sigma-Aldrich

Cobalt, foil, thickness 1.0 mm, 99.95% trace metals basis

GF15401135

Cobalt, foil, light tested, 25x25mm, thickness 0.01mm, 99.9%

326380

Sigma-Aldrich

Cobalt, foil, thickness 0.1 mm, ≥99.99%

GF87130728

Cobalt, wire reel, 0.5m, diameter 0.05mm, hard, 99.9%

GF40808516

Cobalt, foil, 100x100mm, thickness 0.25mm, as rolled, 99.9%

GF75010564

Cobalt, foil, light tested, 25x25mm, thickness 0.0125mm, 99.9%

GF31361835

Cobalt, foil, light tested, 25x25mm, thickness 0.05mm, as rolled, 99.9%

GF39774617

Cobalt, microfoil, disks, 10mm, thinness 0.5μm, specific density 434μg/cm², permanent mylar 3.5μm support, 99.9%

GF95862134

Cobalt, microfoil, disks, 25mm, thinness 0.25μm, specific density 222μg/cm², permanent mylar 3.5μm support, 99.9%

GF74432392

Cobalt, wire reel, 0.1m, diameter 0.05mm, hard, 99.9%

GF53589897

Cobalt, foil, light tested, 25x25mm, thickness 0.015mm, 99.9%

GF84130792

Cobalt, foil, light tested, 25x25mm, thickness 0.025mm, 99.9%

GF08123723

Cobalt, foil, not light tested, 25x25mm, thickness 0.01mm, 99.9%

GF14436503

Cobalt, wire reel, 0.05m, diameter 0.25mm, hard, 99.99+%

GF13124146

Cobalt, foil, not light tested, 100x100mm, thickness 0.02mm, 99.9%

GF15124081

Cobalt, wire reel, 0.1m, diameter 0.5mm, hard, 99.99+%

GF42159315

Cobalt, foil, light tested, 25x25mm, thickness 0.009mm, 99.9%