Anodic TiO2 nanotubular arrays with pre-synthesized hydroxyapatite--an effective approach to enhance the biocompatibility of titanium.

Anodic TiO2 nanotubular arrays with pre-synthesized hydroxyapatite--an effective approach to enhance the biocompatibility of titanium.

Journal of nanoscience and nanotechnology (2013-07-26)

Lu-Ning Wang, Long-Xiang Lin, Chang-Jian Lin, Chen Shen, Alyssa Shinbine, Jing-Li Luo

要旨

Electrochemically anodized TiO2 nanotubular arrays can provide large surface areas for biological species attachment. In order to further enhance the biocompatibility of Ti medical implants, we deposited a pre-synthesized hydroxyapatite inside and on the nanotubular arrays, and examined the biocompatibility of the anodized TiO2 nanotubular arrays with pre-synthesized hydroxyapatite by in vitro assessment in simulated body fluid, and in vitro cell culture. The results showed that the hydroxyapatite coating was able to be induced on TiO2 nanotubular arrays with pre-synthesized hydroxyapatite within 5 days while only a thin film composed of calcium phosphorous chemicals formed on as-formed TiO2 nanotubular arrays. The cell culture evaluation further proved the enhancement of cell attachment and proliferation on TiO2 nanotubular arrays with pre-synthesized hydroxyapatite as opposed to those without pre-synthesized hydroxyapatite. The present study proves that formation of TiO2 nanotubular arrays with pre-synthesized hydroxyapatite a promising method to enhance the biocompatibility of Ti implants.

材料

製品番号

ブランド

製品内容

718467

Sigma-Aldrich

酸化チタン(IV), nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, nanopowder, <25 nm particle size, 99.7% trace metals basis

14027

Sigma-Aldrich

酸化チタン(IV), puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

232033

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, powder, 99.8% trace metals basis

14021

Sigma-Aldrich

酸化チタン(IV), ReagentPlus^®, ≥99%

224227

Sigma-Aldrich

酸化チタン(IV)、ルチル, powder, <5 μm, ≥99.9% trace metals basis

248576

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

酸化チタン(IV)、ルチル, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

酸化チタン(IV)、ルチル型/アナターゼ型混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

366994

Sigma-Aldrich

チタン, powder, <45 μm avg. part. size, 99.98% trace metals basis

348791

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, 99.7% trace metals basis

267503

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.7% trace metals basis

700347

Sigma-Aldrich

酸化チタン(IV)、ルチル型/アナターゼ型混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

268496

Sigma-Aldrich

チタン, powder, −100 mesh, 99.7% trace metals basis

204757

Sigma-Aldrich

酸化チタン(IV)、ルチル, ≥99.98% trace metals basis

204730

Sigma-Aldrich

酸化チタン(IV)、ルチル, 99.995% trace metals basis

677469

Sigma-Aldrich

酸化チタン(IV), contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

460400

Sigma-Aldrich

チタン, wire, diam. 0.25 mm, 99.7% trace metals basis

268526

Sigma-Aldrich

チタン, sponge, 1-20 mm, 99.5% trace metals basis

369489

Sigma-Aldrich

チタン, foil, thickness 2.0 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

チタン, foil, thickness 0.025 mm, 99.98% trace metals basis

04238

Sigma-Aldrich

ヒドロキシアパタイト, puriss., meets analytical specification of Ph. Eur., BP, FCC, E341, ≥90% (calculated on glowed substance)

348805

Sigma-Aldrich

チタン, foil, thickness 0.5 mm, 99.99% trace metals basis

767506

Sigma-Aldrich

チタン, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis

266035

Sigma-Aldrich

チタン, wire, diam. 1.0 mm, 99.99% trace metals basis

305812

Sigma-Aldrich

チタン, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

21223

Sigma-Aldrich

ヒドロキシアパタイト, purum p.a., ≥90% (as Ca₃(PO₄)₂, KT)

460397

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, ≥99.99% trace metals basis

267481

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.99% trace metals basis

635057

Sigma-Aldrich

酸化チタン(IV)、ルチル, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm