Materials for High and Low Refractive Index Coatings

Introduction

Refractive index (RI or n) is of critical importance for photonics applications such as optical waveguides and ophthalmic devices. Based on their unique refractive index characteristics and good optical clarity, polymeric materials are also used as anti-reflective coatings for solar cells, displays and contact lenses.^1,2 With the need for mechanical strength, environmental stability, and ease of processing, polymeric-based materials have the potential to be excellent alternatives to traditional inorganic optical films.³ Other advantages over their inorganic counterparts include light weight, insensitivity to vibrational stress, and low cost. 

Figure 1. Schematic of a display (e.g. LCD) with protective and RI-control polymer overlayer films image

Anti-reflection coatings for LCD displays are one example of an application that uses polymeric RI-control technology (Figure 1). Films of PET (polyethylene terephthalate) or TAC (triacetyl cellulose) are typically applied to protect outer layers of modern multi-layer LCD stacks. PET and TAC are inexpensive strong polymers with n ~ 1.7 much larger than for air (n = 1). A large fraction of light beam incident on an abrupt interface with ?n ~ 0.7 would bounce off (reflect) from the interface. For an LCD, this would result in a significant fraction of ambient light reflected from the display surface, causing glare and wash-out of displayed images. To solve this problem, a light management film stack with gradually varying RI can be applied to the LCD surface. The stack consists of multiple layers with gradually diminishing RI from high adjacent to the PET/TAC surface to low facing air. By matching the refractive index of the display surface to that of air, surface reflection is reduced, leading to higher effective image contrast and reduced washout by ambient reflections.

Zirconium and Hafnium Acrylate Monomers

RI engineering of light management stacks depends on availability of additives to adjust (raise or lower) RI of polymer films. Possible RI-raising additives include metal-oxide nanoparticles and monomers/polymers containing atoms with high (compared to carbon) atomic numbers. Zirconium and hafnium based acrylate monomers newly available in our catalog (Table 1) are particularly well suited for controlling RI of acrylate films, for example urethane acrylates commonly used to formulate protecting films of LCD displays. Cured acrylate films incorporating these products are UV-stable and combine:

• Excellent optical clarity (>95%)
• Good hardness and scratch resistance (>2H Pencil Hardness)
• >Tuning of RI by choosing loading of functional monomer (Figure 2)

Table 1. Polyfunctional zirconium and hafnium acrylate monomers

Product No.	Description	Brand
686239	Zirconium acrylate	Sigma-Aldrich
686247	Zirconium carboxyethyl acrylate 60% (n-propanol)	Sigma-Aldrich
686220	Hafnium carboxyethyl acrylate 60% in 1-butanol, contains 500 ppm methyl hydroquinone as inhibitor	Sigma-Aldrich
686204	Zirconium bromonorbornanelactone carboxylate triacrylate	Sigma-Aldrich

Figure 2. Physical properties of fully cured acrylate films

High and Low RI Polymers

In addition to the polyfunctional zirconium and hafnium acrylates, we offer a range of high RI polymers based on aromatic and brominated aromatic monomers (Table 2), as well as low RI materials based on fluorinated monomers (Table 3). The associated monomers are also available and can be used to synthesize polymers whose refractive index can be tailored. Also listed are UV/thermal crosslinkable polymers for patterning or heterolayered device fabrication. The tables list products sorted in order of refractive index and can be used as material selection tools for your photonics research.

Table 2. High Refractive Index Materials

Name	n4	Tg (°C)4	Homopolymer	Photo Crosslinkable Polymer	Monomer
Poly(pentabromophenyl methacrylate)	1.710	—	592064	591610	592439
Poly(pentabromophenyl acrylate)	—	155	—	591505	592552
Poly(pentabromobenzyl methacrylate)	1.710	—	640301	640298	640336
Poly(pentabromobenzyl acrylate)	1.670	180	640328	—	640263
Poly(vinylphenylsulfide)	1.657	113	640212	—	—
Poly(1-napthyl methacrylate)	1.641	205	640190	—	—
Poly(2-vinylthiophene)	1.638	—	640182	—	—
Poly(2,6-dichlorostyrene)	1.625	167	639974	640174	D74509
Poly(N-vinylphthalimide)	1.620	201	639982	—	349542
Poly(2-chlorostyrene)	1.610	103	640018	—	160679

Table 3. Low Refractive Index Materials

Name	n4,5	Tg (°C)4,5	Homopolymer	Photo Crosslinkable Polymer	Monomer
Poly(1,1,1,3,3,3-hexafluoroisopropyl acrylate)	1.375	-23	630152	—	367656
Poly(2,2,3,3,4,4,4-heptafluorobutyl acrylate)	1.377	-30	630179	—	443751
Poly(2,2,3,3,4,4,4-heptafluorobutyl methacrylate)	1.383	65	591971	592102	444006
Poly(2,2,3,3,3-pentafluoropropyl acrylate)	1.389	-26	630136	—	470961
Poly(1,1,1,3,3,3-hexafluoroisopropyl methacrylate)	1.390	56	591327	591432	367664
Poly(2,2,3,4,4,4-hexafluorobutyl acrylate)	1.394	-22	—	—	474452
Poly(2,2,3,4,4,4-hexafluorobutyl methacrylate)	—	—	—	591874	371971
Poly(2,2,3,3,3-pentafluoropropyl methacrylate)	1.395	70	592080	—	474193
Poly(2,2,2-trifluoroethyl acrylate)	1.411	-10	630098	—	297720
Poly(2,2,3,3-tetrafluoropropyl methacrylate)	1.417	68	591637	—	371998
Poly(2,2,2-trifluoroethyl methacrylate)	1.418	69	—	591750, 591866	373761

1. Oth JFM. 1971. Conformational mobility and fast bond shift in the annulenes. 25(3):573-622. https://doi.org/10.1351/pac197125030573

2. Nalwa H. 2004. Polymer Optical Fibers. American Scientific Publishers.

3. Prasad PN, Williams DJ. 1991. Introduction to Nonlinear Optical Effects in Molecules and Polymers. New York: John Wiley & Sons.

4. Brandrup J, Immergut EH, Grulke EA. 2003. Polymer Handbook. 4. New York: John Wiley & Sons.

5. Gaynor J, Schueneman G, Schuman P, Harmon JP. 1993. Effects of fluorinated substituents on the refractive index and optical radiation resistance of methacrylates. J. Appl. Polym. Sci.. 50(9):1645-1653. https://doi.org/10.1002/app.1993.070500919