  • Enhanced electrochromic coloration of poly(3-hexylthiophene) films by electrodeposited Au nanoparticles.

Enhanced electrochromic coloration of poly(3-hexylthiophene) films by electrodeposited Au nanoparticles.

Journal of nanoscience and nanotechnology (2013-07-19)
Yoon-Chae Nah
PMID23858881
ABSTRACT

Au nanoparticles and poly(3-hexylthiophene) (P3HT) composite films were prepared by electrodeposition of Au nanoparticles using pulse-current electrodeposition followed by the spin coating of P3HT and their enhanced electrochromic coloration was investigated. A relatively uniformed Au nanoparticle was obtained by the controlled electrodeposition on indium tin oxide (ITO) substrate and plasmon absorption band of Au nanoparticles were observed. Optical and electrochemical properties of Au/P3HT composite films were compared with the pure P3HT films. The enhanced electrochromic absorption of the composite films was observed due to the surface plasmon resonance of the Au nanoparticles.

MATERIALS
Product Number
Brand
Product Description
326542
Sigma-Aldrich
Gold, beads, 1-6 mm, 99.999% trace metals basis
326585
Sigma-Aldrich
Gold, powder, <10 μm, ≥99.9% trace metals basis
326526
Sigma-Aldrich
Gold, wire, diam. 0.127 mm, 99.99% trace metals basis
326534
Sigma-Aldrich
Gold, wire, diam. 0.25 mm, ≥99.9% trace metals basis
310980
Sigma-Aldrich
Gold, wire, diam. 0.5 mm, 99.99% trace metals basis
349283
Sigma-Aldrich
Gold, wire, diam. 0.1 mm, 99.99% trace metals basis
349275
Sigma-Aldrich
Gold, foil, thickness 0.05 mm, 99.99% trace metals basis
373168
Sigma-Aldrich
Gold, evaporation slug, diam. × L 0.6 cm × 0.6 cm, 99.99% trace metals basis
349240
Sigma-Aldrich
Gold, foil, thickness 0.25 mm, ≥99.9% trace metals basis
265829
Sigma-Aldrich
Gold, foil, thickness 0.5 mm, 99.99% trace metals basis
265772
Sigma-Aldrich
Gold, powder, <45 μm, 99.99% trace metals basis
265837
Sigma-Aldrich
Gold, rod, diam. 3.0 mm, 99.99% trace metals basis
349305
Sigma-Aldrich
Gold, wire, diam. 1.0 mm, 99.997% trace metals basis
636347
Sigma-Aldrich
Gold, nanopowder, <100 nm particle size, 99.9% trace metals basis
643203
Sigma-Aldrich
Gold coated glass slide, 99.999% (Au), layer thickness 100 Å
643246
Sigma-Aldrich
Gold coated glass slide, 99.999% (Au), layer thickness 1000 Å
643254
Sigma-Aldrich
Gold coated glass cover slip, 99.999% (Au), layer thickness 100 Å, L × W × thickness 22 mm × 22 mm × 130-170 μm, square
265799
Sigma-Aldrich
Gold, wire, diam. 1.0 mm, 99.99% trace metals basis
265780
Sigma-Aldrich
Gold, wire, diam. 0.25 mm, 99.99% trace metals basis
265810
Sigma-Aldrich
Gold, foil, thickness 0.1 mm, 99.99% trace metals basis
268461
Sigma-Aldrich
Gold, foil, thickness 0.025 mm, 99.99% trace metals basis
255734
Sigma-Aldrich
Gold, powder, <850 μm, ≥99.99% trace metals basis
349313
Sigma-Aldrich
Gold, wire, diam. 0.5 mm, 99.999% trace metals basis
326496
Sigma-Aldrich
Gold, foil, thickness 0.127 mm, 99.99% trace metals basis
373184
Sigma-Aldrich
Gold, evaporation slug, diam. × L 0.3 cm × 0.6 cm, 99.99% trace metals basis
643289
Sigma-Aldrich
Gold coated glass cover slip, 99.999% (Au), diam. × thickness 15 mm × 130-170 μm, layer thickness 100 Å