Silver, zinc oxide and titanium dioxide nanoparticle ecotoxicity to bioluminescent Pseudomonas putida in laboratory medium and artificial wastewater.

Silver, zinc oxide and titanium dioxide nanoparticle ecotoxicity to bioluminescent Pseudomonas putida in laboratory medium and artificial wastewater.

Environmental pollution (Barking, Essex : 1987) (2014-09-28)

Florian Mallevre, Teresa F Fernandes, Thomas J Aspray

ABSTRACT

Bacteria based ecotoxicology assessment of manufactured nanoparticles is largely restricted to Escherichia coli bioreporters in laboratory media. Here, toxicity effects of model OECD nanoparticles (Ag NM-300K, ZnO NM-110 and TiO2 NM-104) were assessed using the switch-off luminescent Pseudomonas putida BS566::luxCDABE bioreporter in Luria Bertani (LB) medium and artificial wastewater (AW). IC50 values ∼4 mg L(-1), 100 mg L(-1) and >200 mg L(-1) at 1 h were observed in LB for Ag NM-300K, ZnO NM-110 and TiO2 NM-104, respectively. Similar results were obtained in AW for Ag NM-300K (IC50∼5 mg L(-1)) and TiO2 NM-104 (IC50>200 mg L(-1)) whereas ZnO NM-110 was significantly higher (IC50>200 mg L(-1)). Lower ZnO NM-110 toxicity in AW compared to LB was associated with differences in agglomeration status and dissolution rate. This work demonstrates the importance of nanoecotoxicological studies in environmentally relevant matrices.

MATERIALS

Product Number

Brand

Product Description

295744

Sigma-Aldrich

Silver, wool, diam. 0.05 mm, ≥99.9% trace metals basis

326976

Sigma-Aldrich

Silver, foil, thickness 2.0 mm, 99.9% trace metals basis

265527

Sigma-Aldrich

Silver, foil, thickness 0.1 mm, 99.9% trace metals basis

265586

Sigma-Aldrich

Silver, wire, diam. 0.5 mm, ≥99.99% trace metals basis

265594

Sigma-Aldrich

Silver, wire, diam. 1.0 mm, ≥99.99% trace metals basis

265608

Sigma-Aldrich

Silver, wire, diam. 1.0 mm, 99.9% trace metals basis

265551

Sigma-Aldrich

Silver, wire, diam. 0.127 mm, 99.99% trace metals basis

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

484059

Sigma-Aldrich

Silver, nanopowder, <150 nm particle size, 99% trace metals basis

327050

Sigma-Aldrich

Silver, shot, 1-3 mm, ≥99.99% trace metals basis

348783

Sigma-Aldrich

Silver, wire, diam. 0.1 mm, 99.9% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

369438

Sigma-Aldrich

Silver, foil, thickness 1.0 mm, 99.99% trace metals basis

739421

Sigma-Aldrich

Silver nanowires, diam. × L 50 nm × 6 μm, 0.5% (isopropyl alcohol suspension)

739448

Sigma-Aldrich

Silver nanowires, diam. × L 100 nm × 6 μm, 0.5% (isopropyl alcohol suspension)

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

85131

Sigma-Aldrich

Silver, colloidal, 65-75% Ag basis

265500

Sigma-Aldrich

Silver, powder, <250 μm, 99.99% trace metals basis

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

735825

Sigma-Aldrich

Silver, conductive paste

GF02315247

Silver, wire reel, 20m, diameter 0.125mm, annealed, 99.99%

GF51463357

Titanium, tube, 200mm, outside diameter 10.3mm, inside diameter 8.7mm, wall thickness 0.8mm, annealed, 99.6+%

GF41437830

Titanium, tube, 100mm, outside diameter 1.05mm, inside diameter 0.75mm, wall thickness 0.15mm, annealed, 99.6+%

GF03838282

Titanium, rod, 500mm, diameter 1.5mm, annealed, 99.6+%

GF90963928

Titanium, rod, 25mm, diameter 50mm, 99.99+%

GF35061083

Titanium, tube, 200mm, outside diameter 6.35mm, inside diameter 5.53mm, wall thickness 0.41mm, annealed, 99.6+%

GF48167590

Titanium, tube, 100mm, outside diameter 6.1mm, inside diameter 5.1mm, wall thickness 0.5mm, annealed, 99.6+%