Retentiveness of various luting agents used with implant-supported prosthesis: an in vitro study.

The Journal of oral implantology (2014-12-17)
Pooja Garg, Malesh Pujari, D R Prithviraj, Sumit Khare
ZUSAMMENFASSUNG

Desired retrievability of cemented implant-supported fixed prosthesis makes the retentive strength of cementing agents an important consideration. The aim of the study was to evaluate the retentiveness of purposely designed implant cement and compare its retentiveness with dental cements that are commonly used with implant systems. Ten implant analogs were embedded in auto-polymerizing acrylic resin blocks and titanium abutments were attached to them. Fifty standardized copings were waxed directly on the abutment and casted. The cements used were: (1) resin-bonded zinc oxide eugenol cement, (2) purposely designed implant cement, (3) zinc phosphate cement, (4) zinc polycarboxylate cement, and (5) glass ionomer cement. After cementation, each sample was subjected to a pull-out test using universal testing machine and loads required to remove the crowns were recorded. The mean values and standard deviations of cement failure loads were analyzed using ANOVA and Bonferroni test. The mean values (± SD) of loads at failure (n = 10) for various cements were as follows (N): resin-bonded zinc oxide eugenol cement 394.62 (± 9.76), Premier implant cement 333.86 (± 18.91), zinc phosphate cement 629.30 (± 20.65), zinc polycarboxylate cement 810.08 (± 11.52), and glass ionomer cement 750.17 (± 13.78). The results do not suggest that one cement type is better than another, but they do provide a ranking order of the cements regarding their ability to retain the prosthesis and facilitate easy retrievability.

MATERIALIEN
Produktnummer
Marke
Produktbeschreibung

Sigma-Aldrich
Formaldehyd -Lösung, for molecular biology, 36.5-38% in H2O
SAFC
Formaldehyd -Lösung, contains 10-15% methanol as stabilizer, 37 wt. % in H2O
Sigma-Aldrich
Zinkoxid, ReagentPlus®, powder, <5 μm particle size, 99.9%
Sigma-Aldrich
Zinkoxid, nanopowder, <100 nm particle size
Sigma-Aldrich
Formaldehyd -Lösung, for molecular biology, BioReagent, ≥36.0% in H2O (T)
Sigma-Aldrich
Zinkoxid, puriss. p.a., ACS reagent, ≥99.0% (KT)
Sigma-Aldrich
Eugenol, ReagentPlus®, 99%
Sigma-Aldrich
Formaldehyd -Lösung, ACS reagent, 37 wt. % in H2O, contains 10-15% Methanol as stabilizer (to prevent polymerization)
Sigma-Aldrich
Eugenol, natural, ≥98%, FG
Sigma-Aldrich
Zinkoxid, nanopowder, <50 nm particle size (BET), >97%
Sigma-Aldrich
Zinkoxid, Dispersion, nanoparticles, <100 nm particle size (TEM), ≤40 nm avg. part. size (APS), 20 wt. % in H2O
Supelco
Formaldehyd -Lösung, stabilized with methanol, ~37 wt. % in H2O, certified reference material
Sigma-Aldrich
Zinkoxid, 99.99% trace metals basis
Sigma-Aldrich
Titan, foil, thickness 0.127 mm, 99.7% trace metals basis
Sigma-Aldrich
Titan, powder, <45 μm avg. part. size, 99.98% trace metals basis
Sigma-Aldrich
Zinkoxid, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5% (calc. for dried substance)
Sigma-Aldrich
Titan, foil, thickness 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
Formaldehyd -Lösung, meets analytical specification of USP, ≥34.5 wt. %
Sigma-Aldrich
Eugenol, ≥98%, FCC, FG
Sigma-Aldrich
Zinkphosphat, 99.998% trace metals basis
Sigma-Aldrich
Titan, powder, −100 mesh, 99.7% trace metals basis
Sigma-Aldrich
Zinkoxid, 99.999% trace metals basis
Sigma-Aldrich
Zinkoxid, nanowires, Length 1 um
Sigma-Aldrich
Formaldehyd -Lösung, tested according to Ph. Eur.
Sigma-Aldrich
Titan, sponge, 1-20 mm, 99.5% trace metals basis
Sigma-Aldrich
Titan, wire, diam. 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
Titan, foil, thickness 2.0 mm, 99.7% trace metals basis
Sigma-Aldrich
Titan, foil, thickness 0.025 mm, 99.98% trace metals basis
Titan, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave
Sigma-Aldrich
Titan, foil, thickness 0.5 mm, 99.99% trace metals basis