Aspect ratio dependent fluorescence quenching of eosin Y by gold nanorods.

Aspect ratio dependent fluorescence quenching of eosin Y by gold nanorods.

Journal of nanoscience and nanotechnology (2014-04-18)

Guojun Weng, Jianjun Li, Li Zhang, Junwu Zhao

ABSTRACT

Gold nanorods of different aspect ratios had been synthesized using seed mediated growth method. The formed gold nanorods had been characterized by the absorption and transmission electron microscopy (TEM) measurements. The obtained gold nanorods were used to study the quenched effect on fluorescence of Eosin Y. Experimental results revealed that Eosin Y molecules adsorbed on the metallic surfaces, suffering strong quenching of their fluorescence and the quenching efficiency was different for different aspect ratio. Using dielectric coated gold nanorods model, the probable mechanism of aspect ratio dependent quenching efficiency was obtained by numerical calculation based on fluorescence resonance energy transfer and quasi-static theory. The calculation results showed that the non-monotonic changing of fluorescence quenching was attributed to competing effects of aspect ratio and the dielectric constant of coated shell on surface plasmon resonance.

MATERIALS

Product Number

Brand

Product Description

326542

Sigma-Aldrich

Gold, beads, 1-6 mm, 99.999% trace metals basis

326585

Sigma-Aldrich

Gold, powder, <10 μm, ≥99.9% trace metals basis

230251

Sigma-Aldrich

Eosin Y, 75% (HPLC)

318906

Sigma-Aldrich

Eosin Y solution, 5 wt. % in H₂O

326526

Sigma-Aldrich

Gold, wire, diam. 0.127 mm, 99.99% trace metals basis

326534

Sigma-Aldrich

Gold, wire, diam. 0.25 mm, ≥99.9% trace metals basis

310980

Sigma-Aldrich

Gold, wire, diam. 0.5 mm, 99.99% trace metals basis

349283

Sigma-Aldrich

Gold, wire, diam. 0.1 mm, 99.99% trace metals basis

349275

Sigma-Aldrich

Gold, foil, thickness 0.05 mm, 99.99% trace metals basis

373168

Sigma-Aldrich

Gold, evaporation slug, diam. × L 0.6 cm × 0.6 cm, 99.99% trace metals basis

349240

Sigma-Aldrich

Gold, foil, thickness 0.25 mm, ≥99.9% trace metals basis

265829

Sigma-Aldrich

Gold, foil, thickness 0.5 mm, 99.99% trace metals basis

265772

Sigma-Aldrich

Gold, powder, <45 μm, 99.99% trace metals basis

265837

Sigma-Aldrich

Gold, rod, diam. 3.0 mm, 99.99% trace metals basis

E4009

Sigma-Aldrich

Eosin Y, Dye content ~99 %

E4382

Sigma-Aldrich

Eosin Y disodium salt, certified by the Biological Stain Commission

349305

Sigma-Aldrich

Gold, wire, diam. 1.0 mm, 99.997% trace metals basis

E6003

Sigma-Aldrich

Eosin Y disodium salt, Dye content ≥85 %

GF79016294

Gold, rod, 10mm, diameter 4.0mm, as drawn, 99.95%

GF23782350

Gold, microfoil, disks, 10mm, thinness 0.1μm, specific density 204.1μg/cm², permanent mylar 3.5μm support, 99.99+%

GF18334436

Gold, insulated wire, 1m, conductor diameter 0.075mm, insulation thickness 0.012mm, PTFE (polytetrafluoroethylene) insulation, 99.99%

GF50454132

Gold, insulated wire, 2m, conductor diameter 0.125mm, insulation thickness 0.014mm, polyester insulation, 99.99%

GF38598980

Gold, microfoil, disks, 10mm, thinness 0.5μm, specific density 966μg/cm², permanent mylar 3.5μm support, 99.99+%

GF98812097

Gold, rod, 6mm, diameter 6.0mm, as drawn, 99.95%

GF26034320

Gold, tube, 100mm, outside diameter 10.0mm, inside diameter 9.7mm, wall thickness 0.15mm, as drawn, 99.95%

GF37996789

Gold, tube, 200mm, outside diameter 2.0mm, inside diameter 1.7mm, wall thickness 0.15mm, as drawn, 99.95%

GF33293729

Gold, insulated wire, 0.1m, conductor diameter 0.125mm, insulation thickness 0.016mm, PTFE (polytetrafluoroethylene) insulation, 99.99%

GF47078129

Gold, microleaf disks, 10mm, thinness 0.5μm, specific density 966μg/cm², removable support, 99.99+%

GF43173930

Gold, rod, 25mm, diameter 3.0mm, as drawn, 99.95%

GF73794741

Gold, tube, 200mm, outside diameter 2.0mm, inside diameter 1.8mm, wall thickness 0.1mm, as drawn, 99.95%