Engineering bamboo-type TiO2 nanotube arrays to enhance their photocatalytic property.

Engineering bamboo-type TiO2 nanotube arrays to enhance their photocatalytic property.

Journal of nanoscience and nanotechnology (2014-04-18)

Dongsheng Guan, Paul J Hymel, Chengjun Zhou, Ying Wang

ABSTRACT

Bamboo-type TiO2 nanotube arrays with high surface area can be synthesized by alternating voltage (AV) anodization for their important use as photocatalytic medium. Their morphologies are highly dependent on preparation parameters including anodization time and electrolyte composition. Minimum time of high-voltage steps required for forming desired bamboo ridge spacing on these nanotubes can be calculated from current-time profiles recorded during potentiostatic anodization at the voltage. Water content in NH4F-containing ethylene glycol (EG) electrolytes is optimized simply from analyses of current transients or current-voltage relations for anodization in EG electrolytes with different amount of water, in order to achieve efficient electrochemical growth of TiO2 nanotubes for large ridge density and long tube length. Two types of bamboo-type TiO2 nanotubes with the same length of 5.46 microm but different ridge spacing are synthesized for photocatalytic degradation of methylene blue (MB) under UV radiation. Both of the bamboo-type nanotube arrays show improved photo catalysis compared to smooth TiO2 nanotubes of the same length, due to their larger surface area favorable for heterogeneous catalytic processes. In particular, the apparent rate constant of photocatalytic degradation on bamboo-type nanotubes is up to 29.4% higher than that for degradation on smooth ones.

MATERIALS

Product Number

Brand

Product Description

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

305812

Sigma-Aldrich

Titanium, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

GF91672139

Titanium, wire reel, 20m, diameter 0.05mm, hard, 99.8%

GF43519945

Titanium, wire reel, 2m, diameter 1.0mm, as drawn, 99.99+%

GF34996685

Titanium, wire reel, 200m, diameter 0.125mm, annealed, 99.6+%

GF96391402

Titanium, wire reel, 25m, diameter 0.20mm, annealed, 99.6+%

GF43403431

Titanium, wire reel, 500m, diameter 0.20mm, annealed, 99.6+%

GF36425707

Titanium, wire reel, 200m, diameter 0.20mm, annealed, 99.6+%

GF31085760

Titanium, wire reel, 5m, diameter 0.25mm, as drawn, 99.99+%

GF14377631

Titanium, wire reel, 25m, diameter 0.25mm, annealed, 99.6+%

GF50624434

Titanium, wire reel, 200m, diameter 0.25mm, annealed, 99.6+%

GF46592949

Titanium, wire, straight, 1000mm, diameter 1.0mm, as drawn, 99.6+%

GF00761217

Titanium, wire reel, 200m, diameter 0.25mm, as drawn, 99.6+%

GF84917188

Titanium, wire reel, 1m, diameter 0.25mm, as drawn, 99.99+%

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

GF32801251

Titanium, tube, 1000mm, outside diameter 1.05mm, inside diameter 0.75mm, wall thickness 0.15mm, annealed, 99.6+%

GF25880485

Titanium, tube, 100mm, outside diameter 6.35mm, inside diameter 5.53mm, wall thickness 0.41mm, annealed, 99.6+%