Synthesis and characterization of CoFe2O4/polyaniline nanocomposites for electromagnetic interference applications.

Synthesis and characterization of CoFe2O4/polyaniline nanocomposites for electromagnetic interference applications.

Journal of nanoscience and nanotechnology (2014-04-18)

K Praveena, S Srinath

ABSTRACT

The Cobalt ferrite (CoFe2O4) powders were synthesized by Co-precipitation method. The as prepared ferrite powders were incorporated into a polyaniline matrix at various volumetric ratios. The as prepared composites of ferrite and polyaniline powders were characterized using X-ray diffraction (XRD), transmission electron microscope (TEM). The particle size of CoFe2O4 is found to be 20 nm. The saturation magnetization (M(s)) of all the composites was found to be decreasing with decrease of ferrite content, while coercivity (H(c)) remained at the value corresponding to pure cobalt ferrite nanopowders. The complex permittivity (epsilon' and epsilon") and permeability (mu' and mu") of composite samples were measured in the range of 1 MHz to 1.1 GHz. The value of epsilon' and mu' found to be increased with ferrite volume concentration.

MATERIALS

Product Number

Brand

Product Description

266701

Sigma-Aldrich

Cobalt, wire, diam. 1.0 mm, 99.995% trace metals basis

356891

Sigma-Aldrich

Cobalt, foil, thickness 1.0 mm, 99.95% trace metals basis

266647

Sigma-Aldrich

Cobalt, powder, <150 μm, ≥99.9% trace metals basis

266639

Sigma-Aldrich

Cobalt, powder, 2 μm particle size, 99.8% trace metals basis

203076

Sigma-Aldrich

Cobalt, granular, 99.99% trace metals basis

720712

Sigma-Aldrich

Iron(III) oxide, dispersion, nanoparticles, ≤110 nm particle size, 15 wt. % in ethanol

697745

Sigma-Aldrich

Cobalt, Carbon coated magnetic, nanopowder, <50 nm particle size (TEM), ≥99%

266655

Sigma-Aldrich

Cobalt, pieces, 99.5% trace metals basis

398810

Sigma-Aldrich

Cobalt, rod, diam. 5.0 mm, 99.95% trace metals basis

356867

Sigma-Aldrich

Cobalt, foil, thickness 0.1 mm, 99.95% trace metals basis

GF88007564

Cobalt, foil, not light tested, 50x50mm, thickness 0.02mm, 99.9%

GF46475220

Cobalt, foil, light tested, 50x50mm, thickness 0.05mm, as rolled, 99.9%

GF45144985

Cobalt, foil, not light tested, 100x100mm, thickness 0.007mm, 99.9%

GF44846208

Cobalt, foil, not light tested, 150x150mm, thickness 0.015mm, 99.9%

GF64744937

Cobalt, foil, not light tested, 100x100mm, thickness 0.05mm, as rolled, 99.99+%

GF64339724

Cobalt, foil, not light tested, 100x100mm, thickness 0.008mm, 99.9%

GF45956166

Cobalt, foil, not light tested, 100x100mm, thickness 0.01mm, 99.9%

GF92082012

Cobalt, foil, 8mm disks, thickness 0.05mm, as rolled, 99.99+%

GF89559343

Cobalt, foil, 4mm disks, thickness 0.005mm, 99.9%

GF94077962

Cobalt, foil, 8mm disks, thickness 0.0125mm, 99.9%

GF30716153

Cobalt, foil, 8mm disks, thickness 0.125mm, as rolled, 99.99+%

GF36399437

Cobalt, foil, 6mm disks, thickness 0.25mm, as rolled, 99.9%

GF15928858

Cobalt, foil, not light tested, 25x25mm, thickness 0.008mm, 99.9%

GF40621665

Cobalt, foil, light tested, 50x50mm, thickness 0.0125mm, 99.9%

GF54298233

Cobalt, foil, 8mm disks, thickness 0.015mm, 99.9%

GF08123723

Cobalt, foil, not light tested, 25x25mm, thickness 0.01mm, 99.9%

GF23494608

Cobalt, foil, not light tested, 100x100mm, thickness 0.009mm, 99.9%

GF49928956

Cobalt, foil, 8mm disks, thickness 0.25mm, as rolled, 99.9%

GF10384400

Cobalt, foil, 6mm disks, thickness 0.25mm, as rolled, 99.99+%

GF71622301

Cobalt, foil, not light tested, 25x25mm, thickness 0.0025mm, temporary acrylic support, 99.9%